Microstructure and mechanical properties of hot isostatically pressed zirconia (2 mol% yttria)-reinforced tungsten disilicide composites
Journal Article
·
· Materials Research Bulletin
- Doshisha Univ., Kyoto, Tanabe (Japan)
Dense sintered composites of ZrO{sub 2} (2 mol% Y{sub 2}O{sub 3}) and WSi{sub 2} have been fabricated by hot isostatic pressing for 2 h at 1500 C under 196 MPa. They contain a small amount of W{sub 5}Si{sub 3}; during sintering, WSi{sub 2} decomposes into W{sub 5}Si{sub 3} and amorphous Si. The ZrO{sub 2} Particles in the composites consists of only t-ZrO{sub 2}. Microstructures and mechanical properties are examined, in connection with ZrO{sub 2} content. The fracture toughness and bending strength of the composite with 40 mol% ZrO{sub 2} addition are 7.1 MPa{center_dot}m{sup 1/2} and 1,011 MPa, respectively.
- OSTI ID:
- 99211
- Journal Information:
- Materials Research Bulletin, Vol. 30, Issue 8; Other Information: PBD: Aug 1995
- Country of Publication:
- United States
- Language:
- English
Similar Records
Mechanical properties of hot isostatically pressed zirconia (2 mol% yttria)-reinforced molybdenum disilicide composite
Hot isostatic pressing of TiB{sub 2}-ZrO{sub 2}(2 mol% Y{sub 2}O{sub 3}) composite powders
Strength and phase stability of yttria-ceria-doped tetragonal zirconia/alumina composites sintered and hot isostatically pressed in argon-oxygen gas atmosphere
Journal Article
·
Sat Jul 01 00:00:00 EDT 1995
· Materials Research Bulletin
·
OSTI ID:99211
+2 more
Hot isostatic pressing of TiB{sub 2}-ZrO{sub 2}(2 mol% Y{sub 2}O{sub 3}) composite powders
Journal Article
·
Mon Jul 01 00:00:00 EDT 1996
· Materials Research Bulletin
·
OSTI ID:99211
+1 more
Strength and phase stability of yttria-ceria-doped tetragonal zirconia/alumina composites sintered and hot isostatically pressed in argon-oxygen gas atmosphere
Journal Article
·
Fri Mar 01 00:00:00 EST 1991
· Journal of the American Ceramic Society; (United States)
·
OSTI ID:99211