Diffusion and evaporation of nitrogen on tungsten (100)
Surface diffusion and evaporation from a layer of nitrogen chemisorbed on the (100) plane of tungsten was examined using Auger spectroscopy. The initial localized deposit required for diffusion measurements in a concentration gradient is created by a highly collimated molecular beam. The sample, under computer control, is moved across an electron beam, and the Auger spectra are recorded automatically at different points on the surface. Nitrogen diffusion over the (100) tungsten surface was found to be concentration independent, taking place over a barrier of 28 kcal/mole with a prefactor D/sub 0/ of 3.0 x 10/sup -2/cm/sup -2//sec. At temperatures 900 to 1050 K necessary to observe spreading on the order of 50-100 ..mu..m in the concentration profile, evaporation was found to be a competing process. Therefore, the desorption kinetics of ..beta.. chemisorbed nitrogen on W(100) was studied by a combination of Auger spectroscopy and flash desorption. The activation energy for desorption was found to be 82 kcal/mole with a prefactor of 0.01 molecules/(cm/sup 2/sec). A comparison with the diffusion of nitrogen on the W(110) surface is made, showing for the first time the effect of surface structure on the diffusion of a chemisorbed gas on a solid surface.
- Research Organization:
- Illinois Univ., Urbana (USA)
- OSTI ID:
- 5673008
- Resource Relation:
- Other Information: Thesis (Ph. D.)
- Country of Publication:
- United States
- Language:
- English
Similar Records
Interaction of Hydrogen with Tungsten
KINETIC STUDIES OF THE REACTIONS OCCURRING BETWEEN TUNGSTEN AND GASES AT LOW PRESSURE AND HIGH TEMPERATURES (thesis)
Related Subjects
NITROGEN
DESORPTION
EVAPORATION
TUNGSTEN
SORPTIVE PROPERTIES
SURFACE PROPERTIES
ACTIVATION ENERGY
CHEMISORPTION
HIGH TEMPERATURE
VERY HIGH TEMPERATURE
CHEMICAL REACTIONS
ELEMENTS
ENERGY
METALS
NONMETALS
PHASE TRANSFORMATIONS
SEPARATION PROCESSES
SORPTION
TRANSITION ELEMENTS
360104* - Metals & Alloys- Physical Properties