Dynamic response of concrete beams externally reinforced with carbon fiber reinforced plastic (CFRP) subjected to impulsive loads
- Wright Lab., Eglin AFB, FL (United States). Armament Directorate
- Univ. of Florida, Shalimar, FL (United States). Graduate Engineering and Research Center
A series of 54 laboratory scale concrete beams 3 x 3 x 30 in. in size were impulsively loaded to failure in a drop weight impact machine. The beams had no internal reinforcement, but instead were externally reinforced on the bottom or tension side of the beams with 1, 2, and 3 ply AS4C/1919 graphite epoxy panels. In addition, several of the beams were also reinforced on the sides with 3 ply CFRP. The beams were simply supported in a drop weight machine and subjected to impact loads with amplitudes up to 10 kips, and durations less than 1 ms, at beam midspan. Measurements made during the loading event included beam total load, midspan displacement, as well as midspan strain at 3 locations in the beam`s cross-section. A high speed framing camera was also used to record the beam`s displacement-time behavior as well as to gain insight into the failure mechanisms. Beam midspan accelerations were determined by double differentiation of the displacement versus time data, and in turn, the beam`s inertial loads were calculated using the beam`s equivalent mass. Beam dynamic bending loads versus time were determined from the difference between the total load versus time and the inertial load versus time data. Bending loads versus displacements were also determined along with fracture energies. Failure to correct the loads for inertia will result in incorrect conclusions being drawn from the data, especially for bending resistance of brittle concrete test specimens. A comparison with quasistatic bending (fracture) energy data showed that the dynamic failure energy absorbed by the beams was always less than the static fracture energy, due to the brittle nature of concrete when impulsively loaded.
- OSTI ID:
- 428115
- Report Number(s):
- CONF-960706-; ISBN 0-7918-1772-5; TRN: IM9708%%444
- Resource Relation:
- Conference: American Society of Mechanical Engineers (ASME) pressure vessels and piping conference, Montreal (Canada), 21-26 Jul 1996; Other Information: PBD: 1996; Related Information: Is Part Of Structures under extreme loading conditions -- 1996. PVP-Volume 325; Shin, Y.S. [ed.] [Naval Postgraduate School, Monterey, CA (United States)]; Zukas, J.A. [ed.] [Computational Mechanics Consultants, Inc., Baltimore, MD (United States)]; PB: 272 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Influence of alkali-silica reaction on the shear capacity of reinforced concrete beams with minimum transverse reinforcement
Dynamic crack propagation from a circular defect in a unidirectional carbon fiber reinforced plastic composite [Dynamic crack propagation from a circular defect in a unidirectional CFRP composite]