Synthesis and characterization of new fluoride-containing manganese vanadates A{sub 2}Mn{sub 2}V{sub 2}O{sub 7}F{sub 2} (A=Rb, Cs) and Mn{sub 2}VO{sub 4}F
- Department of Chemistry and Center for Optical Materials Science and Engineering Technologies (COMSET), Clemson University, Clemson, SC 29634-0973 (United States)
- Materials Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, TN 37831 (United States)
- Quantum Condensed Matter Division, Oak Ridge National Laboratory, Oak Ridge, TN 37831 (United States)
Large single crystals of A{sub 2}Mn{sub 2}V{sub 2}O{sub 7}F{sub 2} (A=Rb, Cs) and Mn{sub 2}VO{sub 4}F were grown using a high-temperature (~600 °C) hydrothermal technique. Single crystal X-ray diffraction and powder X-ray diffraction were utilized to characterize the structures, which both possess MnO{sub 4}F{sub 2} building blocks. The A{sub 2}Mn{sub 2}V{sub 2}O{sub 7}F{sub 2} series crystallizes as a new structure type in space group Pbcn (No. 60), Z=4 (Rb{sub 2}Mn{sub 2}V{sub 2}O{sub 7}F{sub 2}: a=7.4389(17) Å, b=11.574(3) Å, c=10.914(2) Å; Cs{sub 2}Mn{sub 2}V{sub 2}O{sub 7}F{sub 2}: a=7.5615(15) Å, b=11.745(2) Å, c=11.127(2) Å). The structure is composed of zigzag chains of edge-sharing MnO{sub 4}F{sub 2} units running along the a-axis, and interconnected through V{sub 2}O{sub 7} pyrovanadate groups. Temperature dependent magnetic susceptibility measurements on this interesting one-dimensional structural feature based on Mn{sup 2+} indicated that Cs{sub 2}Mn{sub 2}V{sub 2}O{sub 7}F{sub 2} is antiferromagnetic with a Neél temperature, T{sub N}=~3 K and a Weiss constant, θ, of −11.7(1) K. Raman and infrared spectra were also analyzed to identify the fundamental V–O vibrational modes in Cs{sub 2}Mn{sub 2}V{sub 2}O{sub 7}F{sub 2}. Mn{sub 2}(VO{sub 4})F crystalizes in the monoclinic space group of C2/c (no. 15), Z=8 with unit cell parameters of a=13.559(2) Å, b=6.8036(7) Å, c=10.1408(13) Å and β=116.16(3)°. The structure is associated with those of triplite and wagnerite. Dynamic fluorine disorder gives rise to complex alternating chains of five-and six-coordinate Mn{sup 2+}. These interpenetrating chains are additionally connected through isolated VO{sub 4} tetrahedra to form the condensed structure. - Graphical abstract: New vanadate fluorides A{sub 2}Mn{sub 2}V{sub 2}O{sub 7}F{sub 2} (A=Rb, Cs) and Mn{sub 2}(VO{sub 4})F have been synthesized hydrothermally. Upon cooling, the one-dimensional Mn(II) substructure results in antiferromagnetic ordering. Display Omitted - Highlights: • Single crystals of A{sub 2}Mn{sub 2}V{sub 2}O{sub 7}F{sub 2}, (A=Rb, Cs) and Mn{sub 2}VO{sub 4}F were grown hydrothermally. • The use of fluoride mineralizers in the synthesis led to the formation of new compounds without OH{sup −} groups. • The structure of A{sub 2}Mn{sub 2}V{sub 2}O{sub 7}F{sub 2} features zigzag chains of MnO{sub 4}F{sub 2} units. • Cs{sub 2}Mn{sub 2}V{sub 2}O{sub 7}F{sub 2} exhibits antiferromagnetic ordering with a Neel temperature of ~3 K. • Mn{sub 2}VO{sub 4}F possesses a condensed framework structure with disordered fluorine atoms.
- OSTI ID:
- 22584192
- Journal Information:
- Journal of Solid State Chemistry, Vol. 241; Other Information: Copyright (c) 2016 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Two halide-containing cesium manganese vanadates: synthesis, characterization, and magnetic properties
A new manganese(II) phosphate templated by ethylenediamine: (C{sub 2}H{sub 10}N{sub 2})[Mn{sub 2}(HPO{sub 4}){sub 3}(H{sub 2}O)]. Hydrothermal synthesis, crystal structure, and spectroscopic and magnetic properties
Related Subjects
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
ANTIFERROMAGNETISM
FLUORIDES
HYDROTHERMAL SYNTHESIS
MAGNETIC SUSCEPTIBILITY
MANGANESE IONS
MANGANESE OXIDES
MONOCLINIC LATTICES
MONOCRYSTALS
NEEL TEMPERATURE
POWDERS
SPACE GROUPS
TEMPERATURE DEPENDENCE
VANADATES
VANADIUM OXIDES
X RADIATION
X-RAY DIFFRACTION