Influence of PbCl{sub 2} content in PbI{sub 2} solution of DMF on the absorption, crystal phase, morphology of lead halide thin films and photovoltaic performance in planar perovskite solar cells
In this paper, the influence of PbCl{sub 2} content in PbI{sub 2} solution of DMF on the absorption, crystal phase and morphology of lead halide thin films was systematically investigated and the photovoltaic performance of the corresponding planar perovskite solar cells was evaluated. The result revealed that the various thickness lead halide thin film with the small sheet-like, porous morphology and low crystallinity can be produced by adding PbCl{sub 2} powder into PbI{sub 2} solution of DMF as a precursor solution. The planar perovskite solar cell based on the 300-nm-thick CH{sub 3}NH{sub 3}PbI{sub 3−x}Cl{sub x} thin film by the precursor solution with the mixture of 0.80 M PbI{sub 2} and 0.20 M PbCl{sub 2} exhibited the optimum photoelectric conversion efficiency of 10.12% along with an open-circuit voltage of 0.93 V, a short-circuit photocurrent density of 15.70 mA cm{sup −2} and a fill factor of 0.69. - Graphical abstract: The figure showed the surface and cross-sectional SEM images of lead halide thin films using the precursor solutions: (a) 0.80 M PbI{sub 2}, (b) 0.80 M PbI{sub 2}+0.20 M PbCl{sub 2}, (c) 0.80 M PbI{sub 2}+0.40 M PbCl{sub 2}, and (d) 0.80 M PbI{sub 2}+0.60 M PbCl{sub 2}. With the increase of the PbCl{sub 2} content in precursor solution, the size of the lead halide nanosheet decreased and the corresponding thin films gradually turned to be porous with low crystallinity. - Highlights: • Influence of PbCl{sub 2} content on absorption, crystal phase and morphology of thin film. • Influence of perovskite film thickness on photovoltaic performance of solar cell. • Lead halide thin film with small sheet-like, porous morphology and low crystallinity. • Planar solar cell with 300 nm-thick perovskite thin film achieved PCE of 10.12%.
- OSTI ID:
- 22573922
- Journal Information:
- Journal of Solid State Chemistry, Vol. 231; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of Oxygen and Water on the Formation and Degradation Processes of (CH3NH3)PbI3 Thin Films
Revealing the Dynamics of Hybrid Metal Halide Perovskite Formation via Multimodal In Situ Probes
Related Subjects
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
ABSORPTION
EFFICIENCY
ELECTRIC POTENTIAL
ELECTRICAL FAULTS
LEAD
LEAD CHLORIDES
LEAD IODIDES
NANOSTRUCTURES
PERFORMANCE
PEROVSKITE
PHOTOVOLTAIC EFFECT
POROUS MATERIALS
POWDERS
PRECURSOR
SCANNING ELECTRON MICROSCOPY
SOLAR CELLS
SOLUTIONS
SURFACES
THICKNESS
THIN FILMS