Further Development of Crack Growth Detection Techniques for US Test and Research Reactors
- Massachusetts Institute of Technology Nuclear Reactor Laboratory (United States)
- Idaho National Laboratory (United States)
One of the key issues facing Light Water Reactors (LWRs) in extending lifetimes beyond 60 years is characterizing the combined effect of irradiation and water chemistry on material degradation and failure. Irradiation Assisted Stress Corrosion Cracking (IASCC), in which a crack propagates in a susceptible material under stress in an aggressive environment, is a mechanism of particular concern. Full understanding of IASCC depends on real time crack growth data acquired under relevant irradiation conditions. Techniques to measure crack growth in actively loaded samples under irradiation have been developed outside the US - at the Halden Boiling Water Reactor, for example. Several types of IASCC tests have also been deployed at the MITR, including passively loaded crack growth measurements and actively loaded slow strain rate tests. However, there is not currently a facility available in the US to measure crack growth on actively loaded, pre-cracked specimens in LWR irradiation environments. A joint program between the Idaho National Laboratory (INL) and the Massachusetts Institute of Technology (MIT) Nuclear Reactor Laboratory (NRL) is currently underway to develop and demonstrate such a capability for US test and research reactors. Based on the Halden design, the samples will be loaded using miniature high pressure bellows and a compact loading mechanism, with crack length measured in real time using the switched Direct Current Potential Drop (DCPD) method. The basic design and initial mechanical testing of the load system and implementation of the DCPD method have been previously reported. This paper presents the results of initial autoclave testing at INL and the adaptation of the design for use in the high pressure, high temperature water loop at the MITR 6 MW research reactor, where an initial demonstration is planned in mid-2015. Materials considerations for the high pressure bellows are addressed. Design modifications to the loading mechanism required by the size constraints of the MITR water loop are described. The safety case for operation of the high pressure gas-driven bellows mechanism is also presented. Key issues are the design and response of systems to limit gas flow in the event of a high pressure gas leak in the in-core autoclave. Integrity of the autoclave must be maintained and reactivity effects due to voiding of the loop coolant must be shown to be within the reactor technical specifications. The technical development of the crack growth monitor for application in the INL Advanced Test Reactor or the MITR can act as a template for adaptation of this technology in other reactors. (authors)
- Research Organization:
- Institute of Electrical and Electronics Engineers - IEEE, 3 Park Avenue, 17th Floor, New York, N.Y. 10016-5997 (United States)
- OSTI ID:
- 22531389
- Report Number(s):
- ANIMMA-2015-IO-342; TRN: US16V0505102330
- Resource Relation:
- Conference: ANIMMA 2015: 4. International Conference on Advancements in Nuclear Instrumentation Measurement Methods and their Applications, Lisboa (Portugal), 20-24 Apr 2015; Other Information: Country of input: France; 1 Ref.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Adaptation of Crack Growth Detection Techniques to US Material Test Reactors
Environmentally assisted cracking in light water reactors - annual report, January-December 2001.
Related Subjects
46 INSTRUMENTATION RELATED TO NUCLEAR SCIENCE AND TECHNOLOGY
BWR TYPE REACTORS
COOLANT LOOPS
CRACK PROPAGATION
DESIGN
DIRECT CURRENT
FAILURES
GAS FLOW
IDAHO NATIONAL LABORATORY
IRRADIATION
LIFETIME
REACTIVITY
RESEARCH REACTORS
STRESS CORROSION
STRESSES
TEST REACTORS