Effect of crystal structure and cationic order on phonon modes across ferroelectric phase transformation in Pb(Fe{sub 0.5-x}Sc{sub x}Nb{sub 0.5})O{sub 3} bulk ceramics
- School of Engineering, Indian Institute of Technology Mandi, 175001, Himachal Pradesh (India)
Pb(Fe{sub 0.5-x}Sc{sub x}Nb{sub 0.5})O{sub 3} [(PFSN) (0 ≤ x ≤ 0.5)] multiferroic relaxors were synthesized and the temperature dependence of phonon modes across ferroelectric to paraelectric transition was studied. With varying Sc content from x = 0 to 0.25 the structure remains monoclinic and with further addition (x = 0.3 - 0.5) the structure transforms into rhombohedral symmetry. Structural refinement studies showed that the change in crystal structure from monoclinic to rhombohedral symmetry involves a volume increment of 34-36%. Associated changes in the tolerance factor (1.024 ≤ t ≤ 0.976) and bond angles were observed. Structure assisted B′-B″ cation ordering was confirmed through the superlattice reflections in selected area electron diffraction (SAED) pattern of Pb(Sc{sub 0.5}Nb{sub 0.5})O{sub 3} (x = 0.5). Cation ordering is also evident from the evolution of Pb-O phonon mode in Raman spectra of compositions with rhombohedral symmetry (x ≥ 0.3). The high temperature Raman scattering studies show that the B-localized mode [F{sub 1u}, ∼250 cm{sup −1}] and BO{sub 6} octahedral rotational mode [F{sub 1g}, ∼200 cm{sup −1}], both originating from polar nano regions (PNRs) behave like coupled phonon modes in rhombohedral symmetry. However, in monoclinic symmetry they behave independently across the transition. Softening of B localized mode across the transition followed by the hardening for all compositions confirms the diffusive nature of the ferroelectric transformation. The presence of correlation between the B localized and BO{sub 6} rotational modes introduces a weak relaxor feature for systems with rhombohedral symmetry in PFSN ceramics, which was confirmed from the macroscopic dielectric studies.
- OSTI ID:
- 22492402
- Journal Information:
- AIP Advances, Vol. 6, Issue 1; Other Information: (c) 2016 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 2158-3226
- Country of Publication:
- United States
- Language:
- English
Similar Records
High-temperature structural transformations in the relaxor ferroelectrics PbSc{sub 0.5}Ta{sub 0.5}O{sub 3} and Pb{sub 0.78}Ba{sub 0.22}Sc{sub 0.5}Ta{sub 0.5}O{sub 3}
Temperature dependent Raman scattering and far-infrared reflectance spectra of MgO modified Pb{sub 0.99}(Zr{sub 0.95}Ti{sub 0.05}){sub 0.98}Nb{sub 0.02}O{sub 3} ceramics: A composition effect
Related Subjects
BOND ANGLE
CATIONS
CERAMICS
CORRELATIONS
ELECTRON DIFFRACTION
FERROELECTRIC MATERIALS
HARDENING
IRON COMPOUNDS
LEAD COMPOUNDS
MONOCLINIC LATTICES
NIOBATES
PHASE TRANSFORMATIONS
PHONONS
RAMAN EFFECT
RAMAN SPECTRA
REFLECTION
SCANDIUM COMPOUNDS
SUPERLATTICES
TEMPERATURE DEPENDENCE
TRIGONAL LATTICES