Determination of transition metal ion distribution in cubic spinel Co{sub 1.5}Fe{sub 1.5}O{sub 4} using anomalous x-ray diffraction
- Indus Synchrotrons Utilization Division, Raja Ramanna Center for Advanced Technology, Indore – 452013 (India)
We report anomalous x-ray diffraction studies on Co ferrite with composition Co{sub 1.5}Fe{sub 1.5}O{sub 4} to obtain the distribution of transition metal ions in tetrahedral and octahedral sites. We synthesize spinel oxide (Co{sub 1.5}Fe{sub 1.5}O{sub 4}) through co-precipitation and subsequent annealing route. The imaginary part (absorption) of the energy dependent anomalous form factor is measured and the real part is calculated theoretically through Kramers–Krönig transformation to analyze anomalous x-ray diffraction peak intensities. Fe and Co K-edge x-ray absorption near edge structure (XANES) spectra are used to estimate charge states of transition metals. Our analysis, within experimental errors, suggests 44% of the tetrahedral sites contain Co in +2 oxidation state and the rest 56% sites contain Fe in +2 and +3 oxidation states. Similarly, 47% of the octahedral sites contain Fe in +3 oxidation states, whereas, the rest of the sites contain Co in +2 and +3 oxidation states. While a distinct pre-edge feature in the Fe K-edge XANES is observed, Co pre-edge remains featureless. Implications of these results to magnetism are briefly discussed.
- OSTI ID:
- 22492297
- Journal Information:
- AIP Advances, Vol. 5, Issue 8; Other Information: (c) 2015 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 2158-3226
- Country of Publication:
- United States
- Language:
- English
Similar Records
Application of x-ray absorption fine structure (XAFS) to local-order analysis in Fe-Cr maghemite-like materials
Local structural variation with oxygen fugacity in Fe2SiO4+x fayalitic iron silicate melts