Title: Calcination temperature influenced multiferroic properties of Ca-doped BiFeO{sub 3} nanoparticles

The influence of Ca-doping and particle size on structural, morphological and magnetic properties of BiFeO{sub 3} nanoparticles has been studied. A sol-gel method was employed for the synthesis of nanoparticles and their particle size was tailored by varying the calcination temperature. Structural analysis revealed a rhombohedral distortion induced by Ca-substitution. The broadening of diffraction peaks with decreasing calcination temperature was indicative of reduction in crystallite size. The morphological analysis revealed the formation of agglomerated nanoparticles having average particle size ranging from 10-15 and 50-55 nm for C4 and C6, respectively. The agglomeration is attributed to high surface energy of nanoparticles. Ferromagnetism has been displayed by all the synthesized nanoparticles. Enhancement of saturation magnetization with Ca-substitution is attributed to suppression of spin cycloid structure by the reduction in size, lattice distortion and creation of oxygen vacancies by the substitution of divalent ion at trivalent site. Further, this value increases as a function of decreasing particle size. Strong particle size effects on magnetic properties of the synthesized nanoparticles are owed to increasing surface to volume ratio. All these observations are indicative of strong dependence of multiferroism on particle size.
Authors:
; ;  [1]
  1. Nano Research Lab, School of Physics and Materials Science, Thapar University, Patiala-147004 (India)
Publication Date:
OSTI Identifier:
22490346
Resource Type:
Journal Article
Resource Relation:
Journal Name: AIP Conference Proceedings; Journal Volume: 1665; Journal Issue: 1; Conference: 59. DAE solid state physics symposium 2014, Tamilnadu (India), 16-20 Dec 2014; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY; BISMUTH COMPOUNDS; CALCINATION; CALCIUM; DIFFRACTION; DOPED MATERIALS; FERRITES; FERROMAGNETISM; MAGNETIC PROPERTIES; MAGNETIZATION; NANOPARTICLES; PARTICLE SIZE; REDUCTION; SOL-GEL PROCESS; SURFACE ENERGY; SURFACES; SYNTHESIS; TEMPERATURE DEPENDENCE; TRIGONAL LATTICES; VACANCIES