Crystallographic orientation variation of isothermal pearlite under high magnetic field
Crystallographic orientation (CO) variation of magnetic-induced pearlite (MIP) during its microstructure evolution in 19.8 T was investigated by electron back-scatter diffraction (EBSD). It is closely related to the isothermal temperatures (ITs) and the applied magnetic time (MT) during the process of MIP formation. The <100> easy magnetization direction in MIP colonies is strengthened with the MT within the certain transformed fraction of MIP (f{sub MIP}) at the relatively lower IT (983 K) above the eutectoid temperature but below the magnetically shifted upward eutectoid temperature, while this special CO tends to be weakened at a relatively higher IT (995 K). For the same MT, the higher the IT, the relatively larger is the proportion in <100> orientation for MIP colonies at the early growth stage. These results have demonstrated that the change of <100> orientation of MIP is closely related to the growth rate of pearlite ferrite (PF), and strengthened mainly at early transformation stage. When f{sub MIP} reaches some value, the growth rate of MIP at other COs, such as <110>, even at the hard magnetization direction, turns to present speed-up. - Highlights: • HMF can induce pearlite with different fractions above the eutectoid temperature. • CO is closely related to isothermal temperatures and applied magnetic time. • <100> direction is related to the growth rate of PF, and strengthened at early stage. • When f{sub MIP} reaches some value, the growth rate at other COs turns to present speed-up.
- OSTI ID:
- 22476107
- Journal Information:
- Materials Characterization, Vol. 105; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 1044-5803
- Country of Publication:
- United States
- Language:
- English
Similar Records
Directional growth of pearlite in iron--carbon eutectoid alloys. [Rate]
A microscopic examination of the precipitation phenomena occurring during the isothermal pearlitic transformation in high carbon-copper nickel steels