Microstructural, mechanical and electrochemical behaviour of a 7017 Al–Zn–Mg alloy of different tempers
The aim of the investigation is to assess the microstructural features and associated physical, mechanical and electrochemical properties of a 7017 Al–Zn–Mg alloy of various tempers. A 7017 Al–Zn–Mg alloy was subjected to different ageing schedules to produce under-(T4), peak-(T6), over-(T7) and highly over-aged tempers. Optical microscopy, hardness measurement, electrical conductivity measurement, tensile testing and SEM fractographs, differential scanning calorimetry (DSC), transmission electron microscopy (TEM), and electrochemical polarization studies have been used to characterize the alloy tempers. Hardness measurement and tensile testing showed the characteristic age hardening phenomenon of aluminium alloys. Optical and TEM micrographs have revealed the variation in size of matrix strengthening η′ (MgZn{sub 2}) and also the size and distribution of grain boundary η (MgZn{sub 2}) precipitate with ageing time. DSC thermograms exhibiting exothermic and endothermic peaks indicated the characteristic solid state reaction sequence of the 7017 alloy. Potentiodynamic polarization study of the 7017 alloy of various tempers in 3.5 wt.% NaCl solution at near neutral pH showed typical active metal dissolution behaviour, but at pH 12 an active–passive–transpassive transition behaviour has been observed. - Graphical abstract: TEM micrograph of the 7017 aluminium alloy of various tempers (a, b) under aged (T4), (c, d) peak aged (T6), (e, f) over aged (T7) and (g, h) highly over-aged. Display Omitted - Highlights: • 7017 Al-Zn-Mg alloy was subjected to different artificial ageing treatments. • Characterization of 7017 alloy tempers by hardness, tensile, DSC, TEM and electrochemical behaviour. • Structure-properties relationship of the 7017 Al-Zn-Mg alloy of various tempers.
- OSTI ID:
- 22476097
- Journal Information:
- Materials Characterization, Vol. 104; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 1044-5803
- Country of Publication:
- United States
- Language:
- English
Similar Records
In-situ formation of Al3Ni nano particles in synthesis of Al 7075 alloy by friction stir processing with Ni powder addition
High-Resolution Electron Microscopy and Kinetic Studies of Precipitation Hardening Reactions in Cast Al-5.8Zn-2.2Mg-2.5Cu
Related Subjects
SUPERCONDUCTIVITY AND SUPERFLUIDITY
AGE HARDENING
ALUMINIUM COMPOUNDS
DISSOLUTION
DISTRIBUTION
ELECTRIC CONDUCTIVITY
ELECTROCHEMISTRY
FRACTOGRAPHY
GRAIN BOUNDARIES
HARDNESS
MAGNESIUM COMPOUNDS
POLARIZATION
PRECIPITATION
SCANNING ELECTRON MICROSCOPY
TENSILE PROPERTIES
TERNARY ALLOY SYSTEMS
TRANSMISSION ELECTRON MICROSCOPY
ZINC COMPOUNDS