Ultrafine nanoporous palladium-aluminum film fabricated by citric acid-assisted hot-water-treatment of aluminum-palladium alloy film
- Department of Materials Science and Technology, Tokyo University of Science, 6-3-1 Niijyuku, Katsushika-ku, Tokyo, 125-8585 (Japan)
Hot-water-treatment has been adapted to fabricate ultrafine nanoporous palladium-aluminum film from aluminum-palladium alloy film. Using citric acid as a chelating agent, a precipitation of boehmite (aluminum oxide hydroxide, AlOOH) on the nanoporous palladium-aluminum film was suppressed. According to cross-sectional scanning transmission electron microscopy observations, the ligament/pore sizes of the prepared nanoporous film were considerably small (on the order of 10 nm). Since this fabrication method only requires aluminum alloy film and hot-water with chelating agent, the ultrafine nanoporous film can be prepared simply and environmentally friendly.
- OSTI ID:
- 22454437
- Journal Information:
- AIP Advances, Vol. 5, Issue 1; Other Information: (c) 2015 Author(s); Country of input: International Atomic Energy Agency (IAEA); ISSN 2158-3226
- Country of Publication:
- United States
- Language:
- English
Similar Records
(Oxy)hydroxides Formed on Aluminum Fuel Materials After Irradiation and Long-Term Wet Storage - 20354
Inhibited Surface Diffusion in Nanoporous Multi-Principal Element Alloy Thin Films Prepared by Vacuum Thermal Dealloying
Thermal Dehydration of Aluminum (Oxy)hydroxides on Fuel Cladding Material - 20200
Conference
·
Wed Jul 01 00:00:00 EDT 2020
·
OSTI ID:22454437
+2 more
Inhibited Surface Diffusion in Nanoporous Multi-Principal Element Alloy Thin Films Prepared by Vacuum Thermal Dealloying
Journal Article
·
Thu Feb 29 00:00:00 EST 2024
· Metals
·
OSTI ID:22454437
Thermal Dehydration of Aluminum (Oxy)hydroxides on Fuel Cladding Material - 20200
Conference
·
Wed Jul 01 00:00:00 EDT 2020
·
OSTI ID:22454437
+2 more