Title: Desilication of ZSM-5 zeolites for mesoporosity development using microwave irradiation

Highlights: • Microwaves have beneficial effects on desilication of zeolites. • Produced mesopores with microwaves have narrow pore-size distribution. • Advantages and disadvantages of various desilicating agents were also reported. - Abstract: Mesoporous ZSM-5 zeolite was obtained by desilication in alkaline solutions with microwave (MW) and conventional electric (CE) heating under hydrothermal conditions. Both methods were effective in the production of mesoporous zeolites; however, MW was more efficient than CE as it led to well-defined mesopores with relatively small sizes and a narrow size distribution within a short treatment time. Moreover, the mesoporous ZSM-5 obtained through this method was effective in producing less bulky products from an acid-catalyzed reaction, specifically the butylation of phenol. Finally, various bases were found to have advantages and disadvantages in desilication. NaOH was the most reactive; however, macroporosity could develop easily under a severe condition. Ammonia water was weakly reactive; however, it could be used to precisely control the pore architecture, and no ion exchange is needed for acid catalysis. Organic amines such as ethylenediamine can also be used in desilication.
Authors:
;  [1] ; ; ;  [2] ;  [1]
  1. Department of Chemistry and Green-Nano Materials Research Center, Kyungpook National University, Daegu 702-701 (Korea, Republic of)
  2. Research Center for Green Catalysis, Division of Green Chemistry and Engineering Research, Korea Research Institute of Chemical Technology, P.O. Box 107, 141 Gajeong-ro, Yuseong, Daejeon 305-600 (Korea, Republic of)
Publication Date:
OSTI Identifier:
22420781
Resource Type:
Journal Article
Resource Relation:
Journal Name: Materials Research Bulletin; Journal Volume: 61; Other Information: Copyright (c) 2014 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; AMINES; AMMONIA; CATALYSIS; CRYSTAL GROWTH; IRRADIATION; MICROWAVE HEATING; MICROWAVE RADIATION; NANOSTRUCTURES; PHENOL; SODIUM HYDROXIDES; SYNTHESIS; ZEOLITES