Piezo-/dielectric properties of perovskite-structure high-temperature relaxor ferroelectrics: The Pb(Lu{sub 1/2}Nb{sub 1/2})O{sub 3}–Pb(Zn{sub 1/3}Nb{sub 2/3})O{sub 3}–PbTiO{sub 3} ternary ceramics
- Key Laboratory of Optoelectronic Materials Chemistry and Physics, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, Fuzhou, Fujian 350002 (China)
Graphical abstract: - Highlights: • Pb(Zn{sub 1/3}Nb{sub 2/3})O{sub 3}-based ternary ferroelectric ceramics were prepared by solid-state synthesis method. • Morphotropic phase boundary region has been determined by XRD, di-/piezoelectric properties. • The compositions near MPB region exhibit excellent piezoelectric properties. - Abstract: A new compositional system of relaxor ferroelectrics was investigated based on the high piezoelectricity Pb(Zn{sub 1/3}Nb{sub 2/3})O{sub 3}–PbTiO{sub 3} ferroelectric perovskite family. Compositions were fabricated near an estimated morphotropic phase boundary (MPB) of the Pb(Lu{sub 1/2}Nb{sub 1/2})O{sub 3}–Pb(Zn{sub 1/3}Nb{sub 2/3})O{sub 3}–PbTiO{sub 3} (PLZNT) ternary system by a two-step synthetic process. Their structures have been analyzed by means of X-ray diffraction technique. On the basis of X-ray powder diffraction, the morphotropic phase boundary (MPB) region for the ternary system was obtained. The Curie temperature T{sub C} of ternary system varied from 240 °C to 330 °C and the coercive fields E{sub c}s > 10 kV/cm. The values of piezoelectric coefficients d{sub 33} vary in the range of 260–450 pC/N with different PZN contents. It is worth noting that the optimum compositions were located at MPB region but near the tetragonal phase. The new PLZNT ceramics exhibit wider range of T{sub C}s and E{sub c}s, making it a promising material for high-powder ultrasound transducers using in a large temperature range.
- OSTI ID:
- 22348601
- Journal Information:
- Materials Research Bulletin, Vol. 51; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Growth and electrical performance of Pb(Mg{sub 1/3}Nb{sub 2/3})O{sub 3}-PbTiO{sub 3}-Pb(Fe{sub 1/2}Nb{sub 1/2})O{sub 3} single crystals
Diffuse transition and piezoelectric properties of Pb[(Zr{sub 1-x}Ti{sub x}){sub 0.74}(Mg{sub 1/3}Nb{sub 2/3}){sub 0.20}(Zn{sub 1/3}Nb{sub 2/3}){sub 0.06}]O{sub 3} Ceramics