Young's modulus and SEM analysis of leg bones exposed to simulated microgravity by hind limb suspension (HLS)
- Department of Physics and Astronomy, University of Central Arkansas, 201 Donaghey Avenue, Lewis Science Center 171, Conway, AR 72035 (United States)
- Department of Applied Science, University of Arkansas at Little Rock, 2801 S. University Avenue, Little Rock, AR 72204 (United States)
- Department of Physiology and Biophysics, University of Arkansas for Medical Sciences, 4301 W. Markham St., Little Rock, AR 72205 (United States)
The aim of this study was to determine composition of the leg bone tissue of rats that were exposed to simulated microgravity by Hind-Limb Suspension (HLS) by tail for one week. The leg bones were cross sectioned, cleaned of soft tissues, dried and sputter coated, and then placed horizontally on the stage of a Scanning Electron Microscope (SEM) for analysis. Interaction of a 17.5 keV electron beam, incident from the vertical direction on the sample, generated images using two detectors. X-rays emitted from the sample during electron bombardment were measured with an Energy Dispersive Spectroscopy (EDS) feature of SEM using a liquid-nitrogen cooled Si(Li) detector with a resolution of 144 eV at 5.9 keV ({sub 25}Mn K{sub {alpha}} x-ray). K{sub {alpha}}- x-rays from carbon, oxygen, phosphorus and calcium formed the major peaks in the spectrum. Relative percentages of these elements were determined using a software that could also correct for ZAF factors namely Z(atomic number), A(X-ray absorption) and F(characteristic fluorescence). The x-rays from the control groups and from the experimental (HLS) groups were analyzed on well-defined parts (femur, tibia and knee) of the leg bone. The SEM analysis shows that there are definite changes in the hydroxyl or phosphate group of the main component of the bone structure, hydroxyapatite [Ca{sub 10}(PO{sub 4}){sub 6}(OH){sub 2}], due to hind limb suspension. In a separate experiment, entire leg bones (both from HLS and control rats) were subjected to mechanical stress by mean of a variable force. The stress vs. strain graph was fitted with linear and polynomial function, and the parameters reflecting the mechanical strength of the bone, under increasing stress, were calculated. From the slope of the linear part of the graph the Young's modulus for HLS bones were calculated and found to be 2.49 times smaller than those for control bones.
- OSTI ID:
- 22116969
- Journal Information:
- AIP Conference Proceedings, Vol. 1525, Issue 1; Conference: 22. international conference on application of accelerators in research and industry, Ft. Worth, TX (United States), 5-10 Aug 2012; Other Information: (c) 2013 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
THE ABSCOPAL EFFECT OF X IRRADIATION ON BONE GROWTH IN RATS
THE EFFECT OF THE GROWTH HORMONE FROM THE ANTERIOR LOBE OF THE PITUITARY ON BONE UNDER CONDITIONS OF IRRADIATION