Structural and magnetic characterization of BiFe{sub x}Mn{sub 2-x}O{sub 5} oxides (x=0.5, 1.0)
- Instituto de Ciencia de Materiales de Madrid, C.S.I.C., Cantoblanco, E-28049 Madrid (Spain)
- Institute for Nuclear Research and Nuclear Energy, Bulgarian Academy of Sciences, 72 Tsarigradsko Chaussee Boulevard, Sofia 1784 (Bulgaria)
- Institut Laue-Langevin, BP156X, Grenoble F-38042 (France)
The title compounds have been synthesized by a citrate technique followed by thermal treatments in air (BiFe{sub 0.5}Mn{sub 1.5}O{sub 5}) or under high oxygen pressure conditions (BiFeMnO{sub 5}), and characterized by X-ray diffraction (XRD), neutron powder diffraction (NPD) and magnetization measurements. The crystal structures have been refined from NPD data in the space group Pbam at 295 K. These phases are isostructural with RMn{sub 2}O{sub 5} oxides (R=rare earths) and contain infinite chains of Mn{sup 4+}O{sub 6} octahedra sharing edges, linked together by (Fe,Mn){sup 3+}O{sub 5} pyramids and BiO{sub 8} units. These units are strongly distorted with respect to those observed in other RFeMnO{sub 5} compounds, due to the presence of the electronic lone pair on Bi{sup 3+}. It is noteworthy the certain level of antisite disorder exhibited in both samples, where the octahedral positions are partially occupied by Fe cations, and vice versa. BiFe{sub x}Mn{sub 2-x}O{sub 5} (x=0.5, 1.0) are short-range magnetically ordered below 20 K for x=0.5 and at 40 K for x=1.0. The main magnetic interactions seem to be antiferromagnetic (AFM); however, the presence of a small hysteresis in the magnetization cycles indicates the presence of some weak ferromagnetic (FM) interactions. - Graphical Abstract: BiFe{sub x}Mn{sub 2-x}O{sub 5} (x=0.5, 1.0) samples are isostructural with BiMn{sub 2}O{sub 5}, belonging to the Pbam space group. The crystal structure contains infinite chains of edge-sharing Mn{sup 4+}O{sub 6} octahedra, interconnected by dimer units of Fe{sup 3+}O{sub 5} square pyramids. These units are strongly distorted due to the presence of the electronic lone pair on Bi{sup 3+}. They are magnetically ordered at low temperatures. The main magnetic interactions seem to be antiferromagnetic with the presence of some weak ferromagnetic response. Highlights: > Two new compounds of formula BiFe{sub x}Mn{sub 2-x}O{sub 5} (x=0.5, 1.0) have been obtained. > Their crystallographic structure is isotypical with that of RMn{sub 2}O{sub 5} materials. > The presence of the electronic lone pair on Bi{sup 3+} severely distorts the crystal structure. > There is no establishment of a long-range ferrimagnetic structure.
- OSTI ID:
- 21580267
- Journal Information:
- Journal of Solid State Chemistry, Vol. 184, Issue 9; Other Information: DOI: 10.1016/j.jssc.2011.07.009; PII: S0022-4596(11)00378-1; Copyright (c) 2011 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
High-pressure synthesis and characterization of BiCu{sub 3}(Mn{sub 4−x}Fe{sub x})O{sub 12} (x=0, 1.0, 2.0) complex perovskites
Structure and magnetic properties of a new anion-deficient perovskite Pb{sub 2}Ba{sub 2}BiFe{sub 4}ScO{sub 13} with crystallographic shear structure
Related Subjects
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
ANTIFERROMAGNETISM
BISMUTH IONS
CRYSTAL STRUCTURE
CRYSTALLOGRAPHY
ELECTRICAL PROPERTIES
HEAT TREATMENTS
INTERACTIONS
IRON IONS
MAGNETIC PROPERTIES
MAGNETIZATION
MANGANESE IONS
NEUTRON DIFFRACTION
OXIDES
RARE EARTHS
SPACE GROUPS
TEMPERATURE RANGE 0065-0273 K
X-RAY DIFFRACTION
CHALCOGENIDES
CHARGED PARTICLES
COHERENT SCATTERING
DIFFRACTION
ELEMENTS
IONS
MAGNETISM
METALS
OXYGEN COMPOUNDS
PHYSICAL PROPERTIES
SCATTERING
SYMMETRY GROUPS
TEMPERATURE RANGE