The Effects of Lithium Triflate (LiCF{sub 3}SO{sub 3}) on the PMMA-based Solid Polymer Electrolytes
- Faculty of Engineering and Science, University Tunku Abdul Rahman, 53300 Kuala Lumpur (Malaysia)
- Faculty of Engineering, Multimedia University, 63100 Cyberjaya (Malaysia)
- Physics Department, University of Malaya, 50603 Kuala Lumpur (Malaysia)
The effects of Lithium triflate salt (LiCF{sub 3}SO{sub 3}), on the poly (methyl methacrylate)(PMMA)-based solid polymer electrolytes plasticized with propylene carbonate (PC) solvated in Tetrahydrofuran (THF) have been studied through a.c impedance spectroscopy and infrared spectroscopy. Lithium triflate was incorporated into the predetermined PMMA/PC system that has the highest value of ionic conductivity. In current investigations, four combination systems: Pure PMMA, (PMMA+PC) systems, (PMMA+LiCF{sub 3}SO{sub 3}) and (PMMA+PC+LiCF{sub 3}SO{sub 3}) systems were prepared using the solution cast method. Solutions were stirred for numerous hours to obtain a homogenous solution before it is poured into the petri dishes under ambient temperature to form the solid electrolyte thin film. The films were then removed from petri discs and transferred into the dessicator for further drying prior to the different tests. From the characterization done through the a.c impedance spectroscopy, the highest room temperature ionic conductivity in the pure PMMA sample, (PMMA+PC) system and (PMMA+LiCF{sub 3}SO{sub 3}) system is 2.83x10{sup -12} Scm{sup -1}, 4.39x10{sup -11} Scm{sup -1} and 3.93x10{sup -6} Scm{sup -1} respectively. The conductivity for (PMMA+PC+LiCF{sub 3}SO{sub 3}) system was obtained with the 30 wt% of lithium triflate, which is 2.48x10{sup -5} Scm{sup -1}. Infrared spectroscopy shows that complexation occurred between the polymer and the plasticizer, and the polymer and plasticizer and salt. The interactions have been studied in the C=O band, C-O-C band and the O-CH{sub 3} band.
- OSTI ID:
- 21371678
- Journal Information:
- AIP Conference Proceedings, Vol. 1217, Issue 1; Conference: ICAMN-2007: International conference on advancement of materials and nanotechnology, Langkawi, Kedah (Malaysia), 29 May - 1 Jun 2007; Other Information: DOI: 10.1063/1.3377823; (c) 2010 American Institute of Physics; ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Preparation and characterization of plasticized palm-based polyurethane solid polymer electrolyte
The Development of a new plasticizer for poly(ethylene oxide) based polymer electrolyte and the investigation of their ion-pair dissociation effect
Related Subjects
37 INORGANIC
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
ABSORPTION SPECTROSCOPY
CARBONIC ACID ESTERS
CERAMICS
DRYING
IMPEDANCE
INFRARED SPECTRA
IONIC CONDUCTIVITY
LITHIUM COMPOUNDS
METHACRYLIC ACID ESTERS
ORGANIC FLUORINE COMPOUNDS
PLASTICIZERS
PMMA
SOLID ELECTROLYTES
SULFONATES
TETRAHYDROFURAN
THIN FILMS
X-RAY DIFFRACTION
ALKALI METAL COMPOUNDS
CARBOXYLIC ACID ESTERS
COHERENT SCATTERING
DIFFRACTION
ELECTRIC CONDUCTIVITY
ELECTRICAL PROPERTIES
ELECTROLYTES
ESTERS
FILMS
FURANS
HETEROCYCLIC COMPOUNDS
ORGANIC COMPOUNDS
ORGANIC HALOGEN COMPOUNDS
ORGANIC OXYGEN COMPOUNDS
ORGANIC POLYMERS
ORGANIC SULFUR COMPOUNDS
PHYSICAL PROPERTIES
POLYACRYLATES
POLYMERS
POLYVINYLS
SCATTERING
SPECTRA
SPECTROSCOPY