A Study of Cavitation Erosion
- Kansai Electric Power Company (Japan)
- Mitsubishi Heavy Industries Ltd. (Japan)
- Japan Atomic Power Company (Japan)
The authors performed experimental study for the purpose of the following two items from a viewpoint of cavitation erosion of a cylindrical orifice in view of a problem at the letdown orifice in PWR (Pressurized Water Reactor). 1. To get the critical cavitation parameter of the cylindrical orifice to establish the design criteria for prevention of cavitation erosion, and 2. to ascertain the erosion rate in such an eventuality that the cavitation erosion occurs with the orifice made of stainless steel with precipitation hardening (17-4-Cu hardening type stainless steel), so that we confirm the appropriateness of the design criteria. Regarding the 1. item, we carried out the cavitation tests to get the critical cavitation parameters inside and downstream of the orifice. The test results showed that the cavitation parameter at inception is independent of the length or the diameter of the orifice. Moreover, the design criteria of cavitation erosion of cylindrical orifices have been established. Regarding the 2. item, we tested the erosion rate under high-pressure conditions. The cavitation erosion actually occurred in the cylindrical orifice at the tests that was strongly resemble to the erosion occurred at the plant. It will be seldom to reproduce resemble cavitation erosion in a cylindrical orifice with the hard material used at plants. We could establish the criteria for preventing the cavitation erosion from the test results. (authors)
- Research Organization:
- The ASME Foundation, Inc., Three Park Avenue, New York, NY 10016-5990 (United States)
- OSTI ID:
- 21070109
- Resource Relation:
- Conference: 10. international conference on nuclear engineering - ICONE 10, Arlington - Virginia (United States), 14-18 Apr 2002; Other Information: Country of input: France
- Country of Publication:
- United States
- Language:
- English
Similar Records
A method to predict cavitation and the extent of damage in power plant piping. Tier 1, Cavitation erosion model: Final report
Cavitation erosion of austenitic stainless steel and effect of boron and nitrogen ion implantation