Crystallographic Study of Mixtures La1+xBa2-xCu3Oy (x=0,0.2,0.4,0.6) after annealing at 860 deg. C
Journal Article
·
· AIP Conference Proceedings
- Department of Physics, Laboratory of Applied Physics, Aristotle University of Thessaloniki (Greece)
- Department of Electrical and Computer Engineering, Aristotle University of Thessaloniki (Greece)
Four powder mixtures with chemical formula La1+xBa2-xCu3Oy was prepared. The mixtures were heated in free atmosphere, at temperature 850 deg. C for 60h and then at 860 deg. C for 40h. XRD measurements were obtained with CuKa radiation. The samples were characterized with the help of the PDF and refined, using the Rietveld's 'Powder Profile Analysis'. Four phases, same for all the samples, were found: (La,Ba)2CuO4, BaCuO2, LaBa2Cu3O7-d, and BaCO3. The percentages of the tour phases are changed, as the x quantity increases, and varied from 38, 25, 18, 19%, for x=0, to 69, 14, 7, 10%, for x=0.6, respectively.
- OSTI ID:
- 21057238
- Journal Information:
- AIP Conference Proceedings, Vol. 899, Issue 1; Conference: 6. international conference of the Balkan Physical Union, Istanbul (Turkey), 22-26 Aug 2006; Other Information: DOI: 10.1063/1.2733398; (c) 2007 American Institute of Physics; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Crystallographic Study of Mixture CeBa1.8Pb0.2Cu3Oy in the Range of 860 deg. C to 940 deg. C
Interactions of Ba{sub 2}YCu{sub 3}O{sub 6+y} with the Gd{sub 3}NbO{sub 7} buffer layer in coated conductors
Unconventional magnetism in ThCr2Si2-type phosphides, La1 xNdxCo2P2
Journal Article
·
Mon Apr 23 00:00:00 EDT 2007
· AIP Conference Proceedings
·
OSTI ID:21057238
Interactions of Ba{sub 2}YCu{sub 3}O{sub 6+y} with the Gd{sub 3}NbO{sub 7} buffer layer in coated conductors
Journal Article
·
Mon Mar 15 00:00:00 EDT 2010
· Journal of Solid State Chemistry
·
OSTI ID:21057238
+2 more
Unconventional magnetism in ThCr2Si2-type phosphides, La1 xNdxCo2P2
Journal Article
·
Wed Jan 01 00:00:00 EST 2014
· Journal of Materials Chemistry C
·
OSTI ID:21057238
+3 more