Synthesis of manganite perovskite Ca{sub 0.5}Sr{sub 0.5}MnO{sub 3} nanoparticles in w/o-microemulsion
Journal Article
·
· Materials Research Bulletin
- Department of Chemistry, TU Berlin, Sekr. TC 8, Strasse des 17. Juni 124, 10623 Berlin (Germany)
In this paper, w/o-microemulsions were employed to produce nanoparticles of the perovskite Ca{sub 0.5}Sr{sub 0.5}MnO{sub 3}, which have a size of approximately 20-50 nm. The procedure was carried out using sodium hydroxide or ammonia as co-precipitation agent. The precursor was transformed to perovskite by calcinations at 580 deg. C. Nanosized particles were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and N{sub 2} adsorption (BET)
- OSTI ID:
- 20891623
- Journal Information:
- Materials Research Bulletin, Vol. 41, Issue 2; Other Information: DOI: 10.1016/j.materresbull.2005.08.015; PII: S0025-5408(05)00317-X; Copyright (c) 2005 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Hydrothermal synthesis of the perovskite manganites Pr{sub 0.5}Sr{sub 0.5}MnO{sub 3} and Nd{sub 0.5}Sr{sub 0.5}MnO{sub 3} and alkali-earth manganese oxides CaMn{sub 2}O{sub 4}, 4H-SrMnO{sub 3}, and 2H-BaMnO{sub 3}
Synthesis and characteristic of nanocrystalline La{sub 0.7}Sr{sub 0.3}MnO{sub 3} manganites by solid state reaction route
Structure, magnetism and transport of the perovskite manganites Ln {sub 0.5}Ca{sub 0.5}MnO{sub 3} (Ln=Ho, Er, Tm, Yb and Lu)
Journal Article
·
Sun May 15 00:00:00 EDT 2005
· Journal of Solid State Chemistry
·
OSTI ID:20891623
Synthesis and characteristic of nanocrystalline La{sub 0.7}Sr{sub 0.3}MnO{sub 3} manganites by solid state reaction route
Journal Article
·
Fri May 06 00:00:00 EDT 2016
· AIP Conference Proceedings
·
OSTI ID:20891623
+1 more
Structure, magnetism and transport of the perovskite manganites Ln {sub 0.5}Ca{sub 0.5}MnO{sub 3} (Ln=Ho, Er, Tm, Yb and Lu)
Journal Article
·
Thu Dec 15 00:00:00 EST 2005
· Journal of Solid State Chemistry
·
OSTI ID:20891623