Ti-6Al-4V electron beam weld qualification using laser scanning confocal microscopy
Journal Article
·
· Materials Characterization
- Aerospace Manufacturing Technology Center, Institute for Aerospace Research, National Research Council, 5145 Decelles Avenue, Montreal, Quebec (Canada)
Processing conditions for manufacturing Ti-6Al-4V components by welding using an electron beam source are known to influence the transformation microstructure in the narrow fusion and heat-affected zones of the weld region. This work examined the effect of multiple-sequence welding on the characteristics of the transformed beta microstructure, using laser scanning confocal microscopy to resolve the Widmanstaetten alpha-beta structure in the fusion zone. The evolution in the alpha interlamellar spacing and plate thickness with processing was then related to microhardness measurements in the weld region.
- OSTI ID:
- 20748745
- Journal Information:
- Materials Characterization, Vol. 54, Issue 3; Other Information: DOI: 10.1016/j.matchar.2004.12.002; PII: S1044-5803(04)00285-2; Copyright (c) 2004 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved; Country of input: International Atomic Energy Agency (IAEA); ISSN 1044-5803
- Country of Publication:
- United States
- Language:
- English
Similar Records
Dissimilar alloy laser beam welding of titanium: Ti-6Al-4V to Beta-C[trademark]. [Ti-3Al-8V-6Cr-4Mo-4Zr]
Direct Observations of Phase Transitions in Ti-6Al-4V Alloy Transient Welds using Time Resolved X-Ray Diffraction
Microstructures and mechanical properties of Ti-6Al-4V welds with filler additions of tantalum and FS85
Journal Article
·
Fri Jul 01 00:00:00 EDT 1994
· Welding Journal (Miami); (United States)
·
OSTI ID:20748745
Direct Observations of Phase Transitions in Ti-6Al-4V Alloy Transient Welds using Time Resolved X-Ray Diffraction
Journal Article
·
Tue Nov 11 00:00:00 EST 2003
· Journal of Applied Physics
·
OSTI ID:20748745
+2 more
Microstructures and mechanical properties of Ti-6Al-4V welds with filler additions of tantalum and FS85
Conference
·
Sat Dec 31 00:00:00 EST 1994
·
OSTI ID:20748745