(110) grain growth and magnetic properties of thin grain-oriented 3% silicon steel sheets
Journal Article
·
· IEEE Transactions on Magnetics (Institute of Electrical and Electronics Engineers)
(110) grain growth and magnetic properties in thin grain-oriented silicon sheets with ultimately low loss were investigated. A final-annealing at 1150 C for 20 min enables us to obtain the thin sheets covered with only (110) grains and consequently the magnetic induction at 800 A/m, B{sub 8} reached 1.9 T.
- Research Organization:
- Nagasaki Univ. (JP)
- OSTI ID:
- 20000779
- Journal Information:
- IEEE Transactions on Magnetics (Institute of Electrical and Electronics Engineers), Vol. 35, Issue 5Pt2; Conference: 1999 international magnetics conference (Intermag '99), Kyongju (KR), 05/18/1999--05/21/1999; Other Information: PBD: Sep 1999; ISSN 0018-9464
- Country of Publication:
- United States
- Language:
- English
Similar Records
Production of ultra thin grain oriented silicon steel sheets
Reduction of iron loss in thin grain-oriented silicon steel sheets
The effect of cold-rolling on the magnetic properties of non-oriented silicon steel sheets
Journal Article
·
Wed Nov 01 00:00:00 EST 1995
· IEEE Transactions on Magnetics
·
OSTI ID:20000779
Reduction of iron loss in thin grain-oriented silicon steel sheets
Journal Article
·
Mon Sep 01 00:00:00 EDT 1997
· IEEE Transactions on Magnetics
·
OSTI ID:20000779
+1 more
The effect of cold-rolling on the magnetic properties of non-oriented silicon steel sheets
Journal Article
·
Wed Sep 01 00:00:00 EDT 1999
· IEEE Transactions on Magnetics (Institute of Electrical and Electronics Engineers)
·
OSTI ID:20000779
+1 more