Effects of the foil flatness on the stress-strain characteristics of U10Mo alloy based monolithic mini-plates
The effects of the foil flatness on stress-strain behavior of monolithic fuel mini-plates during fabrication and irradiation were studied. Monolithic plate-type fuels are a new fuel form being developed for research and test reactors to achieve higher uranium densities. This concept facilitates the use of low-enriched uranium fuel in the reactor. These fuel elements are comprised of a high density, low enrichment, U–Mo alloy based fuel foil encapsulated in a cladding material made of Aluminum. To evaluate the effects of the foil flatness on the stress-strain behavior of the plates during fabrication, irradiation and shutdown stages, a representative plate from RERTR-12 experiments (Plate L1P756) was considered. Both fabrication and irradiation processes of the plate were simulated by using actual irradiation parameters. The simulations were repeated for various foil curvatures to observe the effects of the foil flatness on the peak stress and strain magnitudes of the fuel elements. Results of fabrication simulations revealed that the flatness of the foil does not have a considerable impact on the post fabrication stress-strain fields. Furthermore, the irradiation simulations indicated that any post-fabrication stresses in the foil would be relieved relatively fast in the reactor. While, the perfectly flat foil provided the slightly better mechanical performance, overall difference between the flat-foil case and curved-foil case was not significant. Even though the peak stresses are less affected, the foil curvature has several implications on the strain magnitudes in the cladding. It was observed that with an increasing foil curvature, there is a slight increase in the cladding strains.
- Research Organization:
- Idaho National Lab. (INL), Idaho Falls, ID (United States)
- Sponsoring Organization:
- DOE - NE
- DOE Contract Number:
- DE-AC07-05ID14517
- OSTI ID:
- 1173092
- Report Number(s):
- INL/CON-14-31248
- Resource Relation:
- Conference: International Mechanical Engineering Congress & Exposition,Montreal, CANADA,11/14/2014,11/20/2014
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of the foil flatness on irradiation performance of U10Mo monolithic mini-plates
EFFECTS OF THE FOIL CENTERING ON THE IRRADIATION PERFORMANCE OF U10MO ALLOY BASED MONOLITHIC MINI-PLATES