Title: AgI-MOR Loading Effect on the Durability of the Sandia Low Temperature Sintering GCM Waste Form

Herein, we study the durability of the Sandia Bi-Si oxide Glass Composite Material (GCM) waste form when formulated with different weight percent levels of AgI-MOR. The post-iodine exposure AgI-MOR material was provided to SNL by ORNL. Durability results for the GCM fabricated with 22 and 25% AgI-MOR indicate releases of Ag and I at the same low rates as 15% AgI-MOR GCM, and by the same mechanism. Iodine and Ag release is controlled by the low solubility of an amorphous, hydrated silver iodide, not by the surface-controlled dissolution of I2- loaded Ag-Mordenite. Based on this data, we postulate that much higher loading levels of AgIMOR are probable in this GCM waste form, and limits will govern by retention of mechanical integrity of the GCM versus the solubility of silver iodide.
Authors:
 [1] ;  [1] ;  [1] ;  [1]
  1. Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)
Publication Date:
OSTI Identifier:
1171567
Report Number(s):
SAND2014--17380R
537267
DOE Contract Number:
AC04-94AL85000
Resource Type:
Technical Report
Research Org:
Sandia National Laboratories (SNL-NM), Albuquerque, NM (United States)
Sponsoring Org:
USDOE Office of Nuclear Energy (NE), Fuel Cycle Technologies (NE-5)
Country of Publication:
United States
Language:
English
Subject:
12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE WASTES FROM NUCLEAR FACILITIES