Phase Separation kinetics in an Fe-Cr-Al alloy
- CENIM-CSIC, Madrid, Spain
- ORNL
The {alpha}-{alpha}{prime} phase separation kinetics in a commercial Fe-20 wt.% Cr-6 wt.% Al oxide dispersion-strengthened PM 2000{trademark} steel have been characterized with the complementary techniques atom probe tomography and thermoelectric power measurements during isothermal aging at 673, 708, and 748 K for times up to 3600 h. A progressive decrease in the Al content of the Cr-rich {alpha}{prime} phase was observed at 708 and 748 K with increasing time, but no partitioning was observed at 673 K. The variation in the volume fraction of the {alpha}{prime} phase well inside the coarsening regime, along with the Avrami exponent 1.2 and activation energy 264 kJ mol{sup -1}, obtained after fitting the experimental results to an Austin-Rickett type equation, indicates that phase separation in PM 2000{trademark} is a transient coarsening process with overlapping nucleation, growth, and coarsening stages.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States). Shared Research Equipment Collaborative Research Center
- Sponsoring Organization:
- USDOE Office of Science (SC)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 1045219
- Journal Information:
- Acta Materialia, Vol. 60, Issue 12; ISSN 1359-6454
- Country of Publication:
- United States
- Language:
- English
Similar Records
PHASE SEPARATION IN PM 2000 FE-BASE ODS ALLOY: EXPERIMENTAL STUDY AT THE ATOMIC LEVEL
The - interaction: A study of early stages of phase separation in a Fe-20%Cr-6%Al-0.5%Ti alloy