Dispersion Morphology of Poly(methyl acrylate)/Silica Nanocomposites
Nearly monodisperse poly(methyl acrylate) (PMA) and spherical SiO{sub 2} nanoparticles (NP, d = 14 {+-} 4 nm) were co-cast from 2-butanone, a mutually good solvent and a displacer of adsorbed PMA from silica. The effects of NP content and post-casting sample history on the dispersion morphology were found by small-angle X-ray scattering supplemented by transmission electron microscopy. Analysis of the X-ray results show that cast and thermally annealed samples exhibited a nearly random particle dispersion. That the same samples, prior to annealing, were not well-dispersed is indicative of thermodynamic miscibility during thermal annealing over the range of NP loadings studied. A simple mean-field thermodynamic model suggests that miscibility results primarily from favorable polymer segment/NP surface interactions. The model also indicates, and experiments confirm, that subsequent exposure of the composites to the likely displacer ethyl acetate results in entropic destabilization and demixing into NP-rich and NP-lean phases.
- Research Organization:
- Brookhaven National Lab. (BNL), Upton, NY (United States)
- Sponsoring Organization:
- USDOE SC OFFICE OF SCIENCE (SC)
- DOE Contract Number:
- DE-AC02-98CH10886
- OSTI ID:
- 1042003
- Report Number(s):
- BNL-97681-2012-JA; TRN: US201212%%414
- Journal Information:
- Macromolecules, Vol. 44, Issue 12; ISSN 0024-9297
- Country of Publication:
- United States
- Language:
- English
Similar Records
Properties of na‐montmorillonite and cellulose nanocrystal reinforced poly(butyl acrylate‐co‐methyl methacrylate) nanocomposites
Synthesis of silica coated zinc oxide–poly(ethylene-co-acrylic acid) matrix and its UV shielding evaluation