Near tubule and intertubular bovine detin mapped at the 250 nm level.
- X-Ray Science Division
In this study, simultaneous diffraction and fluorescence mapping with a (250 nm){sup 2}, 10.1 keV synchrotron X-ray beam investigated the spatial distribution of carbonated apatite (cAp) mineral and elemental Ca (and other cations including Zn) around dentin tubules. In 1 {mu}m thick sections of near-pulp root dentin, where peritubular dentin (PTD) is newly forming, high concentrations of Zn, relative to those in intertubular dentin (ITD), were observed adjacent to and surrounding the tubule lumens. Some but not all tubules exhibited hypercalcified collars (high Ca signal relative to the surrounding ITD), and, when present, the zone of high Ca did not extend around the tubule. Diffraction rings from cAp 00.2 and 11.2 + 21.1 + 30.0 reflections were observed, and cAp was the only crystal phase detected. Profiles of Ca, Zn and cAp diffracted intensities showed the same transitions from solid to tubule lumen, indicating the same cAp content and organization in ITD far from the tubules and adjacent to them. Further, the matching Ca and diffraction profiles demonstrated that all of the Ca is in cAp or that any noncrystalline Ca was uniformly distributed throughout the dentin. Variation of 00.2 and 11.2 + 21.1 + 30.0 diffracted intensity was consistent with the expected biaxial crystallographic texture. Extension of X-ray mapping from near 1 {mu}m resolution to the 250 nm level, performed here for dentin and its tubules, will provide new understanding of other mineralized tissues.
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC)
- DOE Contract Number:
- DE-AC02-06CH11357
- OSTI ID:
- 1034261
- Report Number(s):
- ANL/XSD/JA-72087; JSBIEM; TRN: US201203%%475
- Journal Information:
- Journal of Structural Biology, Vol. 176, Issue 2; ISSN 1047-8477
- Country of Publication:
- United States
- Language:
- ENGLISH
Similar Records
Peritubular Dentin Lacks Piezoelectricity
AFM Investigation of mechanical properties of dentin