Heat treatment effects on toughness of 9Cr-1MoVNb and 12Cr-1MoVW steels irradiated at 365{degrees}C
The 9Cr-1MoVNb and 12Cr-1MoVW steels were austenitized at 1040 and 1100{degrees}C to produce different prior austenite grain sizes, after which they were given different tempering treatments (1 h at 760 or 2.5 h at 780{degrees}C). Subsize Charpy impact specimens from these materials were irradiated at 365{degrees}C up to 5 dpa. For 9Cr-1MoVNb steel in the unirradiated condition, the smaller the prior austenite grain size and the higher the tempering temperature, the lower the ductile-brittle transition temperature (DBTT). Regardless of the DBTT in the unirradiated condition, however, the DBTT shift for 9Cr-1MoVNb steel due to irradiation was the same for all heat treatments. This means heat treatment can be used to ensure a lower DBTT before and after irradiation. The 12Cr-1MoVW steel showed little effect of heat treatment on DBTT in the unirradiated condition, and the shift in DBTT was relatively constant. Thus, it appears that heat treatment cannot be used to reduce the effect of irradiation on DBTT for this steel.
- Research Organization:
- Oak Ridge National Lab., TN (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC05-84OR21400
- OSTI ID:
- 10115547
- Report Number(s):
- CONF-911111-32; ON: DE92006592
- Resource Relation:
- Conference: ICFRM-5: 5th. international conference on fusion reactor materials,Clearwater, FL (United States),17-22 Nov 1991; Other Information: PBD: [1991]
- Country of Publication:
- United States
- Language:
- English
Similar Records
Heat treatment effects on impact toughness of 9Cr-1MoVNb and 12Cr-1MoVW steels irradiated to 100 dpa
Void formation and helium effects in 9Cr-1MoVNb and 12Cr-1MoVW steels irradiated in HFIR and FFTF at 400/degree/C
Related Subjects
36 MATERIALS SCIENCE
THERMONUCLEAR REACTOR MATERIALS
PHYSICAL RADIATION EFFECTS
STEEL-CR9MONBV
HEAT TREATMENTS
STEEL-CR12MOV
DUCTILE-BRITTLE TRANSITIONS
MECHANICAL PROPERTIES
GRAIN SIZE
CHARPY TEST
700480
360103
360106
COMPONENT DEVELOPMENT
MATERIALS STUDIES
RADIATION EFFECTS