2 Search Results

Cracking of α-LiAlO₂ matrices in molten carbonate fuel cells (MCFC) leads to reduction in the performance. It was demonstrated in this work that the mechanical strength of α-LiAlO2 matrices is improved by heat-treating at 800°C under ambient gas atmosphere. The mechanical strength (2.91MPa) of the heat-treated matrix was enhanced more than 5 fold compared to the non-heat-treated matrix (0.58MPa). The porosity and crystal structure of the α-LiAlO₂ matrices were not changed after the heat-treatment. The wetting behavior and distribution of carbonate in the heat-treated and the non-heat-treated matrix were investigated and compared. Both non-heat-treated and heat-treated α-LiAlO₂ matrices were completelymore » wetted by molten carbonate. The molten carbonate distribution was concentrated right underneath the circular region formed by the molten carbonate drop in the matrix. Non-heat-treated α-LiAlO₂ samples cracked as a result of the complete absorption of molten carbonate, however, the heat-treated α-LiAlO₂ matrices did not crack, presumably due to their enhanced mechanical strength.« less