Mechanism of the Comonomer Effect in LLDPE from Ethylene/1-Hexene Using a Quinoline-Amine Hafnium Catalyst
Polymers of ethylene and copolymers of ethylene and 1-hexene are synthesized by utilizing a single-site hafnium catalyst activated with tris(pentafluorophenyl)borane. Polymer production increases sharply as compared to the homopolymerization of ethylene with the addition of just a small amount of 1-hexene-a phenomenon known as the "comonomer effect." A mechanism behind the comonomer effect is proposed where the activation-initiation step plays the key part. When only a small fraction of the precatalyst is initially active, high molecular weight (170 000 g mol-1, Đ 1.6) polymer chains grow, forming a physical gel structure that traps catalyst, monomer, and solvent molecules, thereby shutting down the reaction-this scenario plays out in the case of homopolymerization of ethylene. 1-Hexene, when present, slows down the chain growth, thereby lowering the molecular weight and preventing the formation of a gel, which in turn allows for more catalytic sites to be initiated; the reaction continues, resulting in a larger amount of polymer of lower molecular weight (25 000 g mol-1). The proposed mechanism is validated in a series of experiments where targeted variation of the activation/initiation steps is shown to produce, depending on the condition, either a small amount of high molecular weight physical gel or a large amount of low molecular weight polymer.
- Research Organization:
- Argonne National Laboratory (ANL), Argonne, IL (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC), Basic Energy Sciences (BES)
- Grant/Contract Number:
- AC02-06CH11357; AC02-07CH11358
- OSTI ID:
- 2475793
- Journal Information:
- Macromolecules, Journal Name: Macromolecules Journal Issue: 14 Vol. 57; ISSN 0024-9297
- Publisher:
- American Chemical SocietyCopyright Statement
- Country of Publication:
- United States
- Language:
- English
Similar Records
Preparation of high-viscosity, partially hydrolyzed polymethacrylamides
Low stress brittle fracture in polymers: Progress report as of October 23, 1986