The ferromagnetic superconductor Y₉Co₇ was chemically doped to yield the solid solution Y₉Co_7-xPd_x for 0 < x < 0.4. The lattice parameter a does not depend on x, whereas c increases with increasing Pd content up to x = 0.2, the palladium solubility limit. The transition from ferromagnetism (T_C = 4.25 K) to superconductivity (T_sc = 2.4 K) was observed only for the parent Y₉Co₇ compound. For the lowest tested Pd doping level (x = 0.05), ferromagnetism is enhanced strongly (T_C = 9.35 K) and superconductivity is not seen above 1.8 K. Finally, the Curie temperature rapidly increases from 4.25 K to about 10 K for a Pd concentration of x = 0.1 and remains almost unchanged for Y₉Co_6.8Pd_0.2.

• Research Organization: Los Alamos National Laboratory (LANL), Los Alamos, NM (United States)
• Sponsoring Organization: USDOE Office of Science (SC). Basic Energy Sciences (BES) (SC-22)
• Grant/Contract Number: AC52-06NA25396
• OSTI ID: 1454994
• Report Number(s): LA-UR--17-22947
• Journal Information: Intermetallics, Journal Name: Intermetallics Journal Issue: C Vol. 71; ISSN 0966-9795
• Publisher: ElsevierCopyright Statement
• Country of Publication: United States
• Language: English