Helium bubble evolution in ion irradiated Al/B4C metal metrix composite

Zhang, Feifei; Wang, Xu; Wierschke, Jonathan B.; Wang, Lumin

doi:10.1016/j.scriptamat.2015.07.011

Title: Helium bubble evolution in ion irradiated Al/B4C metal metrix composite

Full Record
Other Related Research

Authors:: Zhang, Feifei; Wang, Xu; Wierschke, Jonathan B.; Wang, Lumin

Publication Date:: Tue Dec 01 00:00:00 EST 2015

Sponsoring Org.:: USDOE

OSTI Identifier:: 1251500

Grant/Contract Number:: AC07-05ID14517

Resource Type:: Publisher's Accepted Manuscript

Journal Name:: Scripta Materialia

Additional Journal Information:: Journal Name: Scripta Materialia Journal Volume: 109 Journal Issue: C; Journal ID: ISSN 1359-6462

Publisher:: Elsevier

Country of Publication:: United States

Language:: English

Citation Formats


                    Zhang, Feifei, Wang, Xu, Wierschke, Jonathan B., and Wang, Lumin. Helium bubble evolution in ion irradiated Al/B4C metal metrix composite.  United States: N. p., 2015. 
Web.  doi:10.1016/j.scriptamat.2015.07.011.

Copy to clipboard


                    Zhang, Feifei, Wang, Xu, Wierschke, Jonathan B., & Wang, Lumin. Helium bubble evolution in ion irradiated Al/B4C metal metrix composite.  United States.  https://doi.org/10.1016/j.scriptamat.2015.07.011

Copy to clipboard


                    Zhang, Feifei, Wang, Xu, Wierschke, Jonathan B., and Wang, Lumin. Tue .  
"Helium bubble evolution in ion irradiated Al/B4C metal metrix composite".  United States.  https://doi.org/10.1016/j.scriptamat.2015.07.011.

Copy to clipboard


                    
@article{osti_1251500,

  title        = {Helium bubble evolution in ion irradiated Al/B4C metal metrix composite},

  author       = {Zhang, Feifei and Wang, Xu and Wierschke, Jonathan B. and Wang, Lumin},

  abstractNote = {},

  doi          = {10.1016/j.scriptamat.2015.07.011},

  journal      = {Scripta Materialia},

  number       = C,

  volume       = 109,

  place        = {United States},

  year         = {Tue Dec 01 00:00:00 EST 2015},

  month        = {Tue Dec 01 00:00:00 EST 2015}

}

Copy to clipboard

Journal Article:

Free Publicly Available Full Text

Accepted Manuscript (Publisher)

Publisher's Version of Record
https://doi.org/10.1016/j.scriptamat.2015.07.011

Other availability

Search WorldCat to find libraries that may hold this journal

Citation Metrics:

Cited by: 29 works

Citation information provided by
Web of Science

Save / Share:

Export Metadata

Save to My Library

Similar Records in DOE PAGES and OSTI.GOV collections:

Disordering of helium gas bubble superlattices in molybdenum under ion irradiation and thermal annealing

Journal Article Sun, Cheng ; Gao, Yipeng ; Sprouster, David J. ; ... - Journal of Nuclear Materials

Self-organization of gas bubbles causes the formation of an ordered array of nanoscale gas bubbles (a gas bubble superlattice), a highly efficient mechanism for gas storage under irradiation. Here, the stability of helium (He) gas bubble superlattices in molybdenum (Mo) under krypton (Kr) ion irradiation and thermal annealing has been investigated. The He gas bubble superlattices gradually become disordered under Kr ion irradiation at 300° C, and the order-disorder transformation process completes at 2.5 dpa. Both transmission electron microscopy (TEM) and synchrotron-based small-angle X-ray scattering (SAXS) reveal that the order-disorder transformation of He gas bubble superlattices is associated with amore »« less
https://doi.org/10.1016/j.jnucmat.2020.152315

Full Text Available
The influence of helium on cavity evolution in ion-irradiated T91

Journal Article Monterrosa, Anthony M. ; Jiao, Zhijie ; Was, Gary S. - Journal of Nuclear Materials
https://doi.org/10.1016/j.jnucmat.2018.06.033
Evolution of helium bubbles in aluminum during heavy-ion irradiation

Journal Article Birtcher, R C ; Donnelly, S E ; Templier, C - Physical Review, B: Condensed Matter; (United States)

The evolution of individual He bubbles in thin Al foils during 200-keV Xe irradiation at room-temperature has been followed with [ital in] [ital situ] transmission electron microscopy. He bubbles were produced by room-temperature implantation of 3-keV He ions into prethinned aluminum samples. During subsequent xenon irradiation, several distinct processes were observed to cause individual He bubbles to increase or decrease in size. Bubble growth was observed to take place by radiation-induced coalescence of bubbles without bubble motion. This coalescence was a result of the net displacement of Al atoms out of the volume between bubbles initially in close proximity. Themore »« less
https://doi.org/10.1103/PhysRevB.50.764
In-situ TEM bubble to cavity evolution due to annealing post helium and dual ion irradiation in Cu-10Ta and Cu-3Ta

Journal Article Srinivasan, S. ; Lang, E. ; Burns, K. ; ... - Materials Characterization
https://doi.org/10.1016/j.matchar.2023.113038
Bubble evolution in Kr-irradiated UO₂ during annealing

Journal Article He, L. ; Bai, X. M. ; Pakarinen, J. ; ... - Journal of Nuclear Materials

Transmission electron microscopy observation of Kr bubble evolution in polycrystalline UO₂ annealed at high temperature was conducted in order to understand the inert gas behavior in oxide nuclear fuel. The average size of intragranular bubbles increased gradually from 0.8 nm in as-irradiated sample at room temperature to 2.6 nm at 1600 °C and the bubble size distribution changed from a uniform distribution to a bimodal distribution above 1300 °C. The size of intergranular bubbles increased more rapidly than intragranular ones and bubble denude zones near grain boundaries formed in all the annealed samples. It was found that high-angle grain boundariesmore »« less
Cited by 11
https://doi.org/10.1016/j.jnucmat.2017.09.036

Full Text Available

Similar Records