Sulfur poisoning mechanism of steam reforming catalysts : an X-ray absorption near edge structure (XANES) spectroscopic study.
The present XANES study aims at elucidating the roles of carbon deposits and metal sulfides in the catalyst deactivation in steam reforming reactions with the presence of sulfur. CeO{sub 2}-Al{sub 2}O{sub 3}-supported Ni and Rh-based catalysts were tested in steam reforming of liquid hydrocarbon fuel containing 350 ppm sulfur for H{sub 2} production at 800 C. The Rh catalyst demonstrated much better sulfur tolerance than the Ni catalyst. XANES revealed that there are various sulfur species (metal sulfide, sulfonate, sulfate and organic sulfide) on the used Ni and Rh catalysts. Metal sulfide and organic sulfide are the dominant sulfur species on the Ni catalyst whereas sulfonate and sulfate predominate on the Rh catalyst. Meanwhile organic sulfide and sulfate are also observed on the support alone. Furthermore, there are more carbon deposits formed in the presence of sulfur on both catalysts. More carboxyl groups occur on the carbon deposits formed on the same catalyst when there is no sulfur in the fuel. From correlation analysis of the amounts of nickel sulfide and carbon deposits along with the relative catalytic activity loss, we conclude that sulfur causes the initial deactivation of the Ni catalyst by metal sulfide formation in the first few hours while build-up of carbon deposits contributes mainly to the subsequent deactivation.
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States)
- Sponsoring Organization:
- ONR; USDOE Office of Science (SC); National Science Foundation (NSF)
- DOE Contract Number:
- DE-AC02-06CH11357
- OSTI ID:
- 993396
- Report Number(s):
- ANL/XSD/JA-68409; TRN: US201023%%326
- Journal Information:
- Phys. Chem. Chem. Phys., Vol. 12, Issue Apr. 29, 2010; ISSN 1463-9076
- Country of Publication:
- United States
- Language:
- ENGLISH
Similar Records
Sulfur poisoning of CeO[subscript 2]-Al[subscript 2]O[subscript 3]-supported mono- and bi-metallic Ni and Rh catalysts in steam reforming of liquid hydrocarbons at low and high temperatures
Influence of Sulfur on the Carbon Deposition in Liquid Hydrocarbon Steam Reforming over CeO2-Al2O3 supported Ni and Rh Catalysts