Mechanical properties of hot isostatically pressed zirconia (2 mol% yttria)-reinforced molybdenum disilicide composite
Journal Article
·
· Materials Research Bulletin
- Doshisha Univ., Kyoto, Tanabe (Japan)
- Taiyo Koko Co. Ltd., Hyogo, Ako (Japan)
Dense sintered composites of ZrO{sub 2} (2 mol% Y{sub 2}O{sub 3}) and MoSi{sub 2} have been fabricated by hot isostatic pressing for 2 h at 1400 C under 196 MPa. The ZrO{sub 2} particles in the composites consist of only t-ZrO{sub 2}. There is no reaction between ZrO{sub 2} and MoSi{sub 2}. Microstructures and mechanical properties are examined, in connection with increased ZrO{sub 2} content. The fracture toughness and bending strength of the composite with 40 mol% ZrO{sub 2} addition are 6.18 MPa{center_dot}m{sup 1/2} and 1034 MPa, respectively.
- OSTI ID:
- 99247
- Journal Information:
- Materials Research Bulletin, Vol. 30, Issue 7; Other Information: PBD: Jul 1995
- Country of Publication:
- United States
- Language:
- English
Similar Records
Microstructure and mechanical properties of hot isostatically pressed zirconia (2 mol% yttria)-reinforced tungsten disilicide composites
Hot isostatic pressing of TiB{sub 2}-ZrO{sub 2}(2 mol% Y{sub 2}O{sub 3}) composite powders
Strength and phase stability of yttria-ceria-doped tetragonal zirconia/alumina composites sintered and hot isostatically pressed in argon-oxygen gas atmosphere
Journal Article
·
Tue Aug 01 00:00:00 EDT 1995
· Materials Research Bulletin
·
OSTI ID:99247
+1 more
Hot isostatic pressing of TiB{sub 2}-ZrO{sub 2}(2 mol% Y{sub 2}O{sub 3}) composite powders
Journal Article
·
Mon Jul 01 00:00:00 EDT 1996
· Materials Research Bulletin
·
OSTI ID:99247
+1 more
Strength and phase stability of yttria-ceria-doped tetragonal zirconia/alumina composites sintered and hot isostatically pressed in argon-oxygen gas atmosphere
Journal Article
·
Fri Mar 01 00:00:00 EST 1991
· Journal of the American Ceramic Society; (United States)
·
OSTI ID:99247