Effect of Low Temperature Irradiation in ATR On The Mechanical Properties of Ternary V-Cr-Ti Alloys
Book
·
OSTI ID:984283
Tensile tests and shear punch teats were performed on a variety of vanadium alloys that were irradiated in the Advanced Test Reactor (ATR) at temperatures between 200 and 300 degrees C to doses between 3 and 5 dpa. Tests were performed at room temperature and the irradiation temperature. The results of both the tensile tests and the shear punch tests show that following low temperature irradiation, the yield strength increased by a factor of 3-4 while the ultimate strength increased by a factor of approximately 3.
- Research Organization:
- Pacific Northwest National Laboratory (PNNL), Richland, WA (US)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 984283
- Report Number(s):
- PNNL-SA-31871; AT6020100
- Country of Publication:
- United States
- Language:
- English
Similar Records
On High-Fluence Irradiation Hardening of Nine RPV Surveillance Steels in the UCSB ATR-2 Experiment: Implications for Extended-Life Embrittlement Predictions
Shear Punch Testing on ATR Irradiated MA956 FeCrAl Alloy
COMPRESSION TESTING OF V-4Cr-4Ti
Book
·
Thu Jun 01 00:00:00 EDT 2023
·
OSTI ID:1993668
Shear Punch Testing on ATR Irradiated MA956 FeCrAl Alloy
Technical Report
·
Tue Jun 13 00:00:00 EDT 2017
·
OSTI ID:1363743
COMPRESSION TESTING OF V-4Cr-4Ti
Book
·
Tue Sep 30 00:00:00 EDT 2008
·
OSTI ID:1328080