Influence of molecular ordering on electrical and friction properties of omega-(trans-4-stilbene)alkylthiol self-assembled monolayers on Au (111)
The electrical and friction properties of omega-(trans-4-stilbene)alkylthiol self-assembled monolayers (SAMs) on Au(111) were investigated using atomic force microscopy (AFM) and near edge x-ray absorption fine structure spectroscopy (NEXAFS). The sample surface was uniformly covered with a molecular film consisting of very small grains. Well-ordered and flat monolayer islands were formed after the sample was heated in nitrogen at 120 oC for 1 h. While lattice resolved AFM images revealed a crystalline phase in the islands, the area between islands showed no order. The islands exhibit substantial reduction (50percent) in friction, supporting the existence of good ordering. NEXAFS measurements revealed an average upright molecular orientation in the film, both before and after heating, with a narrower tilt-angle distribution for the heated fim. Conductance-AFM measurements revealed a two orders of magnitude higher conductivity on the ordered islands than on the disordered phase. We propose that the conductance enhancement is a result of a better pi-pi stacking between the trans-stilbene molecular units as a result of improved ordering in islands.
- Research Organization:
- Lawrence Berkeley National Lab. (LBNL), Berkeley, CA (United States)
- Sponsoring Organization:
- Materials Sciences Division
- DOE Contract Number:
- DE-AC02-05CH11231
- OSTI ID:
- 983242
- Report Number(s):
- LBNL-3386E; LANGD5; TRN: US201014%%435
- Journal Information:
- Langmuir, Journal Name: Langmuir; ISSN 0743-7463
- Country of Publication:
- United States
- Language:
- English
Similar Records
Photoisomerization and photodimerization in self-assembled monolayers of cis- and trans-4-cyano-4`-(10-mercaptodecoxy)stilbene on gold
Generation of defects in model lubricant monolayers and their contribution to energy dissipation in friction