Superlattice Coatings for Device, Structural and Protective Applications
Conference
·
OSTI ID:982013
Thin film superlattice materials can exhibit physical, optical and mechanical properties very different and superior to those of single layer counterparts. In the past fifteen years, hard coating, optical and electrical device technologies have advanced beyond the use of single layer coatings with the development of nanoscale compositionally modulated coatings, or superlattices and nanocomposites. A typical superlattice consists of hundreds to thousands of nm-scale layers with alternating compositions and/or crystalline phases. It is possible to engineer the electrical and mechanical properties by choice of layer thicknesses and compositions. Typical layer thicknesses are between 2 and 100 nm. We report of three types of superlattice coatings: (1) AlN/Si3N4 optical superlattice for abrasion protection of ZnS IR windows, (2) Al/Cu structural superlattices and (3) advanced thermoelectric superlattices. All superlattice coatings were deposited by DC and RF reactive magnetron sputtering. The AlN/Si3N4 superlattice had layer thicknesses of 2 nm and exhibited a nanohardness of 35 GPa. The Al/Cu superlattice had layer thicknesses of 1.5 nm and a hardness near 6.5 GPa and is being developed for lightweight optics for space applications. The thermoelectric superlattice demonstrated a figure of merit (ZT) ~ 1.5 and is being developed for power generation from waste heat sources.
- Research Organization:
- Pacific Northwest National Laboratory (PNNL), Richland, WA (US)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 982013
- Report Number(s):
- PNNL-SA-51747; 830403000
- Country of Publication:
- United States
- Language:
- English
Similar Records
Magnetron-Sputtered Nanolaminate and Superlattice Coatings
Enhanced hardness in epitaxial TiAlScN alloy thin films and rocksalt TiN/(Al,Sc)N superlattices
Conditions of Attaining a Superhard State at a Critical Thickness of Nanolayers in Multiperiodic Vacuum-Arc Plasma Deposited Nitride Coatings
Conference
·
Sun Jul 01 00:00:00 EDT 2007
·
OSTI ID:912512
Enhanced hardness in epitaxial TiAlScN alloy thin films and rocksalt TiN/(Al,Sc)N superlattices
Journal Article
·
Mon Oct 13 00:00:00 EDT 2014
· Applied Physics Letters
·
OSTI ID:22350891
Conditions of Attaining a Superhard State at a Critical Thickness of Nanolayers in Multiperiodic Vacuum-Arc Plasma Deposited Nitride Coatings
Journal Article
·
Sun Jan 14 23:00:00 EST 2018
· Technical Physics Letters
·
OSTI ID:22786585