Effects of Fast Neutron Irradiation on Zirconium Carbide
- ORNL
High-purity zone refined zirconium carbide has been fast neutron irradiated in the dose and temperature range of 1-10 x 10{sup 25} N/m{sup 2} (E > 0.1 MeV) and 635-1480 C, respectively. Non-irradiated and as-irradiated properties were measured including the lattice parameter, hardness and elastic modulus as determined through nano-indentation, thermal conductivity, and indentation fracture toughness. The effects of neutron irradiation on the microstructure were also determined though using transmission electron microscopy. The general finding of this paper, limited to this particular zone refined ZrC of nominal C/Zr ratio of 0.93, is that this ceramic is quite stable under neutron irradiation in the temperature and dose range studied. Measurement of lattice parameter before and after irradiation indicated a lack of significant crystalline strain due to irradiation. Only modest changes were observed in the mechanical properties of hardness, elastic modulus, and indentation fracture toughness. The thermal conductivity underwent a slight reduction near 1000 C irradiation, though was essentially unchanged for 1300-1480 C irradiation. Transmission electron microscopy revealed black-spot-type defects (likely Frank or other small loops) for irradiation at 670 C, maturing to faulted Frank loops at 1280 C. As the irradiation temperature increased from 1280 C to the highest irradiation temperature, of 1496 C, a transition to prismatic loops occurs.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States). High Flux Isotope Reactor (HFIR); Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States). High Temperature Materials Lab. (HTML); Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States). Shared Research Equipment Collaborative Research Center
- Sponsoring Organization:
- USDOE Office of Nuclear Energy (NE)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 979284
- Journal Information:
- Journal of Nuclear Materials, Vol. 399, Issue 2-3; ISSN 0022-3115
- Country of Publication:
- United States
- Language:
- English
Similar Records
Mechanical- and physical-property changes of neutron-irradiated chemical-vapor-deposited silicon carbide
Microstructural Defects in SiC Neutron Irradiated at Very High Temperatures