Ageing of a phosphate ceramic used to immobilize chloride contaminated actinide waste
AWE has developed a process for the immobilization of ILW waste containing a significant quantity of chloride using Ca3(PO4)2 as the host material. Waste ions are incorporated into two phosphate based phases, chlorapatite, Ca5(PO4)3Cl, and spodiosite, Ca2(PO4)Cl. Non-active trials performed at AWE using samarium as the actinide surrogate demonstrated the durability of these phases in aqueous solution. Trials of the process using actinide-doped material were performed at PNNL which confirmed the immobilized wasteform resistant to aqueous leaching. Initial leach trials conducted on 239Pu /241Am loaded ceramic at 40°C/28 days gave normalized mass losses of 1.2 x 10-5 g.m-2 and 2.7 x 10-3 g.m-2 for Pu and Cl respectively. In order to assess the response of the phases to radiation-induced damage, accelerated ageing trials were performed on samples in which the 239Pu was replaced by 238Pu. No changes to the crystalline structure of the waste were detected using XRD after the samples had experienced a radiation dose of 4 x 1018 α.g-1. Leach trials showed that there had been an increase in the P and Ca release rates but no change in the Pu release rate.
- Research Organization:
- Pacific Northwest National Lab. (PNNL), Richland, WA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 977322
- Report Number(s):
- PNNL-SA-60313; 830403000
- Journal Information:
- Journal of Nuclear Materials, 385(2):485-488, Journal Name: Journal of Nuclear Materials, 385(2):485-488
- Country of Publication:
- United States
- Language:
- English
Similar Records
Ageing of a phosphate ceramic used to immobilize chloride-contaminated actinide waste
Preparation and Characterization of a Calcium Phosphate Ceramic for the Immobilization of Chloride-containing Intermediate Level Waste