Transverse texture and microstructure gradients in friction-stir welded 2519 aluminum.
- John F.
- Richard W.
Friction-stir welding produces severe thermomechanical transients that generate crystallographic texture evolution throughout the weld-affected microstructure . In this study, a friction stir weld in a coarse-grained 2519 aluminum plate was investigated in order to resolve the influence of these thermal and deformation effects on texture and microstructure development . Automated electron backscatter diffraction (EBSD) was applied to spatially resolve orientations in the base metal, weld nugget, and thermomechanical and heat-affected zones. Results show a gradient demarcated by an alteration in boundary character, texture, and precipitate distribution between the thermomechanical affected zone and the recrystallized weld nugget . EBSD scans and microstructural characterizations reveal substructure evolution from the base plate to the nugget indicative of dynamic recovery and recrystallization processes . Experimental results of texture evolution, however, did not directly follow from considerations of simplified deformation gradients and resultant simple shear textures resulting from restricted glide .
- Research Organization:
- Los Alamos National Laboratory
- Sponsoring Organization:
- DOE
- OSTI ID:
- 976560
- Report Number(s):
- LA-UR-03-1103
- Country of Publication:
- United States
- Language:
- English
Similar Records
Microstructure and texture evolution of friction stir lap welded dissimilar multi-aluminum stack
Texture and precipitation behavior of friction stir welded Inconel 825 alloy