Verification of Allowable Stresses In ASME Section III Subsection NH For Grade 91 Steel & Alloy 800H
- ASME Standards Technology, LLC
The database for the creep-rupture of 9Cr-1Mo-V (Grade 91) steel was collected and reviewed to determine if it met the needs for recommending time-dependent strength values, S{sub t}, for coverage in ASME Section III Subsection NH (ASME III-NH) to 650 C (1200 F) and 600,000 hours. The accumulated database included over 300 tests for 1% total strain, nearly 400 tests for tertiary creep, and nearly 1700 tests to rupture. Procedures for analyzing creep and rupture data for ASME III-NH were reviewed and compared to the procedures used to develop the current allowable stress values for Gr 91 for ASME II-D. The criteria in ASME III-NH for estimating S{sub t} included the average strength for 1% total strain for times to 600,000 hours, 80% of the minimum strength for tertiary creep for times to 600,000 hours, and 67% of the minimum rupture strength values for times to 600,000 hours. Time-temperature-stress parametric formulations were selected to correlate the data and make predictions of the long-time strength. It was found that the stress corresponding to 1% total strain and the initiation of tertiary creep were not the controlling criteria over the temperature-time range of concern. It was found that small adjustments to the current values in III-NH could be introduced but that the existing values were conservative and could be retained. The existing database was found to be adequate to extend the coverage to 600,000 hours for temperatures below 650 C (1200 F).
- Research Organization:
- ASME Standards Technology, LLC.
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- FC07-05ID14712
- OSTI ID:
- 974278
- Report Number(s):
- DOE/ID14712-1
- Country of Publication:
- United States
- Language:
- English
Similar Records
Progress Report on Alloy 617 Time Dependent Allowables
A Review & Assessment of Current Operating Conditions Allowable Stresses in ASME Section III Subsection NH
CAN COVERAGE OF ALLOY 800H IN ASME SECTION III SUBSECTION NH BE EXTENDED TO 850?C?
Technical Report
·
Mon Jun 01 00:00:00 EDT 2015
·
OSTI ID:1236836
A Review & Assessment of Current Operating Conditions Allowable Stresses in ASME Section III Subsection NH
Technical Report
·
Sun Dec 13 23:00:00 EST 2009
·
OSTI ID:974283
CAN COVERAGE OF ALLOY 800H IN ASME SECTION III SUBSECTION NH BE EXTENDED TO 850?C?
Conference
·
Sat Dec 31 23:00:00 EST 2005
·
OSTI ID:965817