Condition monitoring methods applied to degradation of chlorosulfonated polyethylene cable jacketing materials.
Three promising polymer material condition monitoring (CM) methods were applied to eight commercial chlorosulfonated polyethylene cable jacket materials aged under both elevated temperature and high-energy radiation conditions. The CM methods examined, cross-sectional modulus profiling, solvent uptake and NMR T{sub 2} relaxation time measurements of solvent-swelled samples, are closely related since they are all strongly influenced by the changes in overall crosslink density of the materials. Each approach was found to correlate well with ultimate tensile elongation measurements, the most widely used method for following degradation of elastomeric materials. In addition approximately universal failure criteria were found to be applicable for the modulus profiling and solvent uptake measurements, independent of the CSPE material examined and its degradation environment. For an arbitrarily assumed elongation 'failure' criterion of 50% absolute, the CSPE materials typically reached 'failure' when the modulus increased to {approx}35 MPa and the uptake factor in p-xylene decreased to {approx}1.6.
- Research Organization:
- Sandia National Laboratories (SNL), Albuquerque, NM, and Livermore, CA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 972138
- Report Number(s):
- SAND2005-3251J; TRN: US201007%%127
- Journal Information:
- Proposed for publication in Polymer Degradation and Stability., Journal Name: Proposed for publication in Polymer Degradation and Stability.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Activation Energies of Harvested Boston Insulated Wire and Okonite Cable Materials
Investigation of Bonded Jacket Cable Insulation Failure Mechanisms: HELB Environment Results