Low Temperature Age Hardening in U-13 at.% Nb: An Atom Probe Tomography Study
Journal Article
·
· Journal of Nuclear Materials
- Los Alamos National Laboratory (LANL)
- ORNL
- University of Leeds, UK
Low temperature aging (<350 C) of U-13 at.% Nb martensite results in increased strength levels accompanied by significant ductility loss. To determine the decomposition mechanism(s) responsible for these mechanical property changes, atom probe tomography was used to examine the niobium and impurity distributions after aging at 200 or 300 C for times ranging from 2 h to 70 days. No patterns of niobium or impurity atoms were observed that would indicate segregation to the martensitic twin interfaces, making this hardening mechanism unlikely. Phase separation into roughly equiaxed regions of high and low niobium concentration was clearly observed after aging at 300 C for 70 days. However, only subtle niobium concentration changes were observed after aging at 200 C relative to the as-quenched condition, indicating that conventional phase separation is an unlikely explanation for the dramatic mechanical property changes at 200 C. Therefore, consideration of aging mechanisms other than segregation and phase separation may be warranted.
- Research Organization:
- Oak Ridge National Laboratory (ORNL); Shared Research Equipment Collaborative Research Center
- Sponsoring Organization:
- SC USDOE - Office of Science (SC)
- DOE Contract Number:
- AC05-00OR22725
- OSTI ID:
- 962988
- Journal Information:
- Journal of Nuclear Materials, Journal Name: Journal of Nuclear Materials Journal Issue: 2 Vol. 393; ISSN 0022-3115; ISSN JNUMAM
- Country of Publication:
- United States
- Language:
- English
Similar Records
Carbon Redistribution and Carbide Precipitation in a High-Strength Low-Carbon HSLA-115 Steel Studied on a Nanoscale by Atom Probe Tomography
Spinodal Ordering and Precipitation in U-6 wt% Nb
Effect of small additions of oxygen and nitrogen on the nature of the mechanical properties-temperature relationship in niobium
Journal Article
·
Tue May 09 00:00:00 EDT 2017
· Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science
·
OSTI ID:1373785
Spinodal Ordering and Precipitation in U-6 wt% Nb
Conference
·
Sun Dec 18 23:00:00 EST 2005
·
OSTI ID:891382
Effect of small additions of oxygen and nitrogen on the nature of the mechanical properties-temperature relationship in niobium
Journal Article
·
Sun Dec 31 23:00:00 EST 1972
· Probl. Prochnosti, no. 6, pp. 54-56
·
OSTI ID:4350225