Characterization of twinning in electrodeposited Ni-Mn alloys.
Twinning is ubiquitous in electroplated metals. Here, we identify and discuss unique aspects of twinning found in electrodeposited Ni-Mn alloys. Previous reports concluded that the twin boundaries effectively refine the grain size, which enhances mechanical strength. Quantitative measurements from transmission electron microscopy (TEM) images show that the relative boundary length in the as-plated microstructure primarily comprises twin interfaces. Detailed TEM characterization reveals a range of length scales associated with twinning beginning with colonies ({approx}1000 nm) down to the width of individual twins, which is typically <50 nm. We also consider the connection between the crystallographic texture of the electrodeposit and the orientation of the twin planes with respect to the plating direction. The Ni-Mn alloy deposits in this work possess a 110-fiber texture. While twinning can occur on {l_brace}111{r_brace} planes either perpendicular or oblique to the plating direction in {l_brace}110{r_brace}-oriented grains, plan-view TEM images show that twins form primarily on those planes parallel to the plating direction. Therefore, grains enclosed by twins and multiply twinned particles are produced. Another important consequence of a high twin density is the formation of large numbers of twin-related junctions. We measure an area density of twin junctions that is comparable to the density of dislocations in a heavily cold-worked metal.
- Research Organization:
- Sandia National Laboratories
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 959097
- Report Number(s):
- SAND2004-3005J
- Journal Information:
- Proposed for publication in Philosophical Magazine A., Journal Name: Proposed for publication in Philosophical Magazine A.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Dynamic behavior of twins in BaTiO{sub 3}
Grain boundary segregation in {l_angle}110{r_angle} symmetrical tilt bicrystals of an Fe-3%Si alloy