Studies of Degraded Smelt Spout Opening Tubes
- ORNL
- Paprican
Co-extruded type 304L stainless steel/SA210 carbon steel tubes have been used on the floors and lower walls of many black liquor recovery boilers to address the wall thinning problem that had been an issue for boiler owners and operators. Use of these tubes greatly reduced the corrosion issue, but corrosion was still sometimes observed and cracking was discovered in some tubes, particularly those that are bent to form the openings for smelt spouts. Because cracks in the opening tubes were sometimes observed to extend a significant distance into the tube wall and because these cracks were found fairly frequently, tubes made from a number of alternate cladding materials were tried in place of the 304L clad opening tubes. This paper describes the results of examinations of spout opening tubes of the standard 304L/carbon steel and of several of the alternate materials that have been tried. In addition to the corrosion and cracking seen in the spout opening tubes, another issue associated with these tubes has been observed. Preferential corrosion of the cap welds is sometimes seen on butt welds attaching the spout opening tubes made with alternate cladding materials to the standard 304L/carbon steel co-extruded wall tubes. Some information on the observations of this corrosion is also included in this paper.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE Office of Energy Efficiency and Renewable Energy (EERE)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 958771
- Resource Relation:
- Conference: Corrosion 2007, Nashville, TN, USA, 20070311, 20070315
- Country of Publication:
- United States
- Language:
- English
Similar Records
Overview of the DOE studies of recovery boiler floor tube cracking
Final Report, Materials for Industrial Heat Recovery Systems, Tasks 3 and 4 Materials for Heat Recovery in Recovery Boilers