Direct Correlation of CdTe Solar Cell Stabiity with Mobile Ion Charge Generation During Accelerated Lifetime Testing: Preprint
Conference
·
OSTI ID:958250
CdS/CdTe cells deposited on CTO/ZTO TCO substrates show greater degradation than similar devices fabricated on cSnO2/iSnO2 substrates.
- Research Organization:
- National Renewable Energy Laboratory (NREL), Golden, CO.
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC36-99GO10337
- OSTI ID:
- 958250
- Report Number(s):
- NREL/CP-520-46055
- Country of Publication:
- United States
- Language:
- English
Similar Records
Degradation and Capacitance-Voltage Hysteresis in CdTe Devices: Preprint
High-Efficiency CTO/ZTO/CdS/CdTe Polycrystalline Thin-Film Solar Cells: Preprint
CdS/CdTe Thin-Film Solar Cell with a Zinc Stannate Buffer Layer
Conference
·
Wed Jul 01 00:00:00 EDT 2009
·
OSTI ID:962017
High-Efficiency CTO/ZTO/CdS/CdTe Polycrystalline Thin-Film Solar Cells: Preprint
Conference
·
Mon Oct 01 00:00:00 EDT 2001
·
OSTI ID:15000038
CdS/CdTe Thin-Film Solar Cell with a Zinc Stannate Buffer Layer
Conference
·
Tue Oct 27 23:00:00 EST 1998
·
OSTI ID:6608
Related Subjects
14 SOLAR ENERGY
36 MATERIALS SCIENCE
BACK CONTACT
CADMIUM
CAPACITANCE-VOLTAGE
CU DIUFFSION
FILL FACTOR
HYSTERESIS
ION CHARGE GENERATION
LIFETIME
ORIGIN
OXIDES
PERFORMANCE
PROCESSING
PV
RELIABILITY
SCANNING ELECTRON MISCROSCOPY
SOLAR CELL
SOLAR CELLS
STABILITY
STANNATES
SUBSTRATES
Solar Energy - Photovoltaics
TESTING
ZINC
36 MATERIALS SCIENCE
BACK CONTACT
CADMIUM
CAPACITANCE-VOLTAGE
CU DIUFFSION
FILL FACTOR
HYSTERESIS
ION CHARGE GENERATION
LIFETIME
ORIGIN
OXIDES
PERFORMANCE
PROCESSING
PV
RELIABILITY
SCANNING ELECTRON MISCROSCOPY
SOLAR CELL
SOLAR CELLS
STABILITY
STANNATES
SUBSTRATES
Solar Energy - Photovoltaics
TESTING
ZINC