Two-dimensional metal-insulator transition and in-plane magnetoresistance in a high mobility strained Si quantum well.
- Universitat Linz, Institut fur Halbleiterphysik, Linz, Austria
- Princeton University, Princeton, NJ
The apparent metal-insulator transition is observed in a high-quality two-dimensional electron system (2DES) in the strained Si quantum well of a Si/Si{sub 1-x}Ge{sub x} heterostructure with mobility {mu} = 1.9 x 10{sup 5} cm{sup 2}/V s at density n = 1.45 x 10{sup 11} cm{sup -2}. The critical density, at which the thermal coefficient of low T resistivity changes sign, is -0.32 x 10{sup 11} cm{sup -2}, a very low value obtained in Si-based 2D systems. The in-plane magnetoresistivity {rho}(B{sub ip}) was measured in the density range, 0.35 x 10{sup 11} < n < 1.45 x 10{sup 11} cm{sup -2}, where the 2DES shows the metallic-like behavior. It first increases and then saturates to a finite value {rho}(B{sub c}) for B{sub ip}>B{sub c} , with B{sub c} the full spin-polarization field. Surprisingly, {rho}(B{sub c})/{rho}(0)-1.8 for all the densities, even down to n = 0.35 x 10{sup 11} cm{sup -2}, only 10% higher than n{sub c}. This is different from that in clean Si metal-oxide-semiconductor field-effect transistors, where the enhancement is strongly density dependent and {rho}(B{sub c})/{rho}(0) appears to diverge as n {yields} n{sub c}. Finally, we show that in the fully spin-polarized regime, dependent on the 2DES density, the temperature dependence of {rho}(B{sub ip}) can be either metallic-like or insulating.
- Research Organization:
- Sandia National Laboratories
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 952150
- Report Number(s):
- SAND2005-0643J
- Journal Information:
- Proposed for presentation at the Physical Review B., Journal Name: Proposed for presentation at the Physical Review B.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Charge transport in the fractional quantum Hall liquid to Wigner solid transition regime
Enhancement of the colossal magnetoresistance in Eu{sub 1-x}Ca{sub x}B{sub 6}