Mechanical Properties of Neutron Irradiated Nano-structured Ferritic Alloy 14YWT
Conference
·
OSTI ID:951917
- ORNL
Advanced nano-structured ferritic alloys (NFAs) containing a high density of ultra-fine (2-5 nm) nanoclusters enriched in Y, Ti, and O are considered promising candidates for structural components in future nuclear systems. The microstructure of a NFA is composed of nanometer sized regions rich in Y, Ti, and O uniformly distributed in a ferritic matrix. The high number density of nanoclusters in NFAs are responsible for their superior tensile strengths compared to conventional ODS ferritic alloys and may provide effective trapping centers for point defects and transmutation products produced during neutron irradiation. This paper summarizes the mechanical properties of an advanced NFA, designated 14YWT, currently being developed at Oak Ridge National Laboratory. For this study an identical alloy to 14YWT, designated 14WT, was produced without nanocluster dispersions in order to quantify the effect of the nanoclusters on mechanical properties. This report summarizes preliminary tensile and fracture toughness data for 14YWT and 14WT irradiated at 300, 580, and 670 to ~1.5 displacements per atom.
- Research Organization:
- Oak Ridge National Laboratory (ORNL); High Flux Isotope Reactor; Shared Research Equipment Collaborative Research Center
- Sponsoring Organization:
- SC USDOE - Office of Science (SC)
- DOE Contract Number:
- AC05-00OR22725
- OSTI ID:
- 951917
- Country of Publication:
- United States
- Language:
- English
Similar Records
Summary of Previous Mechanical Test Data on ODS Alloys 14YWT and OFRAC up to 1000ºC
In Situ Synchrotron Tensile Investigations on 14YWT, MA957 and 9-Cr ODS Alloys
Temperature effect of elastic anisotropy and internal strain development in advanced nanostructured alloys: An in-situ synchrotron X-ray investigation
Technical Report
·
Sat May 01 04:00:00 UTC 2021
·
OSTI ID:1784108
In Situ Synchrotron Tensile Investigations on 14YWT, MA957 and 9-Cr ODS Alloys
Conference
·
Fri Jan 01 04:00:00 UTC 2016
·
OSTI ID:1265557
Temperature effect of elastic anisotropy and internal strain development in advanced nanostructured alloys: An in-situ synchrotron X-ray investigation
Journal Article
·
Sat Apr 01 04:00:00 UTC 2017
· Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing
·
OSTI ID:1373890