Interfacial sliding stress in Si{sub 3}N{sub 4}/BN fibrous monoliths.
Journal Article
·
· Scr. Materialia
Pushout tests of Si{sub 3}N{sub 4} cells in Si{sub 3}N{sub 4}/BN fibrous monoliths yielded values for debond and sliding stresses of 45{+-}8 and 25{+-}7 MPa, respectively. The sliding stress was consistent with estimates of residual stresses and the interfacial friction coefficient.
- Research Organization:
- Argonne National Laboratory (ANL)
- Sponsoring Organization:
- DOD; NATO
- DOE Contract Number:
- AC02-06CH11357
- OSTI ID:
- 949309
- Report Number(s):
- ANL/ET/JA-39817
- Journal Information:
- Scr. Materialia, Journal Name: Scr. Materialia Journal Issue: 10 ; May 24, 2002 Vol. 46; ISSN 1359-6462; ISSN SCMAF7
- Country of Publication:
- United States
- Language:
- ENGLISH
Similar Records
High-temperature compressive deformation of Si{sub 3}N{sub 4}/BN fibrous monoliths.
Mechanical property characterization of multidirectional Si{sub 3}N{sub 4}/BN fibrous monoliths.
Effect of processing variables on interfacial properties of an SiC-fiber-reinforced reaction-bonded Si[sub 3]N[sub 4] matrix composite
Conference
·
Wed Feb 03 23:00:00 EST 1999
·
OSTI ID:10938
Mechanical property characterization of multidirectional Si{sub 3}N{sub 4}/BN fibrous monoliths.
Conference
·
Tue Jun 29 00:00:00 EDT 1999
·
OSTI ID:11174
Effect of processing variables on interfacial properties of an SiC-fiber-reinforced reaction-bonded Si[sub 3]N[sub 4] matrix composite
Journal Article
·
Sat Oct 01 00:00:00 EDT 1994
· Journal of the American Ceramic Society; (United States)
·
OSTI ID:6765187