Transmission Electron Microscope Study on Electrodeposited Gd2O3 and Gd2Zr2O7 Buffer Layers forYBa2Cu307-..delta.. Superconductors
We have investigated the microstructures of electrodeposited Gd{sub 2}O{sub 3} (GO) and Gd{sub 2}Zr{sub 2}O{sub 7} (GZO) buffer layers for YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} (YBCO) superconductors with conventional transmission electron microscopy (TEM). A high density of nanoscale voids was present in the GZO buffer layers. No voids were observed in GO buffer layers grown on GZO. YBCO superconductor grown on the GO/GZO buffer layer structure produced a critical current density (J{sub c}) of 3.3 x 10{sup 6} A/cm{sup 2} at 77 K in zero field.
- Research Organization:
- National Renewable Energy Laboratory (NREL), Golden, CO.
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC36-99GO10337
- OSTI ID:
- 940613
- Journal Information:
- Physica C, Journal Name: Physica C Journal Issue: 2008 Vol. 468
- Country of Publication:
- United States
- Language:
- English
Similar Records
Electrodeposited Gd2Zr2O7 and Gd2O3 Buffer Layers for YBa2Cu3O7-..delta.. Superconductors
Electrodeposited Biaxially Textured Buffer Layers for YBCO Superconductors
LaNiO(3) Buffer Layers for High Critical Current Density YBa(2)Cu(3)O(7-delta) and Tl(2)Ba(2)CaCu(2)O(8-delta) Films
Journal Article
·
Sun Dec 31 23:00:00 EST 2006
· Journal of Electronic Materials
·
OSTI ID:978489
Electrodeposited Biaxially Textured Buffer Layers for YBCO Superconductors
Conference
·
Mon Jun 01 00:00:00 EDT 2009
·
OSTI ID:968193
LaNiO(3) Buffer Layers for High Critical Current Density YBa(2)Cu(3)O(7-delta) and Tl(2)Ba(2)CaCu(2)O(8-delta) Films
Journal Article
·
Tue Aug 24 00:00:00 EDT 1999
· Applied Physics Letters
·
OSTI ID:10190